Surface treatment process for zinc sulfide lens

A surface treatment, zinc sulfide technology, applied in chemical instruments and methods, cleaning methods using tools, cleaning methods using liquids, etc., to improve the yield, avoid scrap and repair probability, and improve the pass rate.

Pending Publication Date: 2022-07-29
安徽光智科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the above-mentioned problems existing in the prior art, the purpose of the present invention is to provide a zinc sulfide lens surface treatment process, which can better clean the zinc sulfide lens, and solve the dirty and whitish appearance of the zinc sulfide lens surface after coating problem, improve the yield of zinc sulfide lens production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface treatment process for zinc sulfide lens
  • Surface treatment process for zinc sulfide lens
  • Surface treatment process for zinc sulfide lens

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] like figure 1 As shown, for the polished D45.6 zinc sulfide lens, this embodiment provides a surface treatment process for the zinc sulfide lens, including the following steps:

[0040] (1) Wipe with an aqueous solution of citric acid after polishing. In the aqueous solution of citric acid, the mass ratio of citric acid to water is 1:5, the purity of the citric acid is 99%, and the water is deionized water. During the wiping process, wrap the index finger with a dust-free cloth, drip the aqueous solution of citric acid on the index finger, and gently wipe the lens evenly in one direction until the surface of the lens is observed under a strong light, and the surface is free of dirt. The cleanliness level of the dust-free cloth is not lower than 100. During the wiping process of the dust-free cloth, it is necessary to keep the wiping part of the dust-free cloth without wrinkles and the surface is smooth;

[0041] (2) Configuring a polishing liquid, the polishing liquid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of lens surface treatment, and discloses a surface treatment process of a zinc sulfide lens, which comprises the following steps: (1) citric acid wiping; (2) preparing a polishing solution; (3) wiping with a polishing solution; (4) ultrasonic cleaning; and (5) entering a subsequent film coating procedure after the inspection is qualified. According to the zinc sulfide lens surface treatment process, the zinc sulfide lens can be better cleaned, the appearance problems that the surface of the zinc sulfide lens is dirty and white after film coating and the like are solved, and the yield of the zinc sulfide lens in the production process is increased.

Description

technical field [0001] The invention belongs to the field of infrared product surface treatment, and more particularly relates to a surface treatment process for zinc sulfide lenses. Background technique [0002] Zinc sulfide lens is mainly used as the mainstream product of infrared lens. It has excellent band characteristics and can penetrate visible waves to medium and long wavelengths. Surveillance, vehicle infrared night vision, fire protection, power detection, etc. have huge applications. [0003] Zinc sulfide lenses are coated before delivery, and undergo surface treatment before coating. The current common surface treatment process is: after polishing, use a clean cloth dipped in alcohol and acetone to wipe by hand before coating. The process has the following problems: [0004] (1) When wiping by hand, excessive wiping may be performed to remove visible dirt on the surface. In the specific wiping process, the alcohol / acetone wiping time is too long and the wiping ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B08B3/12B08B3/08B08B1/00C09G1/02
CPCB08B3/12B08B3/08C09G1/02B08B1/143B08B1/30
Inventor 欧琳芳朱刘赖永艳彭乔刘开友刘克武梁献波陈丽婷顾迎春吴承伟
Owner 安徽光智科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com