Production method for raising nitrogen content of granular complex fertilizer

A compound fertilizer and manufacturing method technology, applied in the direction of fertilizer form, fertilizer mixture, fertilization device, etc., can solve the problems of difficult production, uneven particle size, low granulation rate, etc., achieve no three wastes discharge, and reduce the requirement for vacuum degree , particle smooth effect

Inactive Publication Date: 2005-03-30
SHANGHAI RES INST OF CHEM IND
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is extremely difficult for some systems (especially sulfur-based compound fertilizers) to produce NPK compound fertilizers with high nitrogen content
Mainly there are defects such as low granulation rate and uneven particle size under high nitrogen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for raising nitrogen content of granular complex fertilizer
  • Production method for raising nitrogen content of granular complex fertilizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Take 200kg of urea solution from the outlet of the first stage of the evaporator separator in the urea production plant and pass it into the drum. The concentration of the urea solution itself is about 96%, the temperature is about 138°C, and the pressure is about 0.5MPa. Put 800kg of compound fertilizer in the drum in advance, and its formula is N-P 2 o 5 -K 2 O=10-17.5-17.5, particle diameter is 1-3mm. The drum rotates, and the lifting board on the drum wall lifts the low-nitrogen compound fertilizer from the bottom of the drum to the upper part of the drum, and the fertilizer particles fall onto the tray by gravity, forming a uniformly distributed curtain of fertilizer particles through the tray. The rotational speed of the drum was 4 rpm, and the inclination angle θ of the drum was 2°. The flight board is an inclined flight board, and the α angle of the flight board is 135°.

[0029] The urea solution passed into the drum is sprayed from the nozzle in the drum t...

Embodiment 2

[0031] In addition to taking 371kg of urea solution at the outlet of the first stage of the evaporator separator in the urea production plant, 629kg of compound fertilizer is preset in the drum. The rotating speed of the drum is 16 rpm, and the inclination angle θ of the drum is 6°. The α angle of the inclined shape lifting board is 140 °, all the other operating steps and process parameters are the same as embodiment 1, finally obtain 1000kg of compound fertilizers that improve nitrogen content, and its compounding formula is N-P 2 o 5 -K 2 O=22.5-11.25-11.25, the strength of the fertilizer particles is greater than 40 Newton / particle, and the moisture increment is not greater than 0.2%.

Embodiment 3

[0033] Take 196kg of solid urea, heat it to 140°C to make it a urea solution, add 4kg of water, pressurize it to about 0.5MPa through a urea melt pump, filter it through a filter equipped with a 200-mesh filter, and put it into the drum. It is equipped with a pressure nozzle, and the urea solution is sprayed from the nozzle, atomized into about 200 mesh or finer droplets, and evenly coated on the fertilizer particle curtain formed by the pre-added compound fertilizer. The amount of compound fertilizer added in advance is 800kg, and its formula is N-P 2 o 5 -K 2 O=10-17.5-17.5, particle diameter is 1-3mm. The rotational speed of the drum was 10 rpm, and the inclination angle θ of the drum was 8°. The flight board is an inclined flight board, and the α angle of the flight board is 135°. Obtain 1000kg of compound fertilizers that increase nitrogen content at last, and its compounding formula is N-P 2 o 5 -K 2 O=17.4-14-14, the strength of the fertilizer particles is greate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The production method for raising nitrogen content of granular composite mixed fertilzier includes the following steps: firstly, feeding the fertilizer into rotary drum, using lifting plate to lift the fertilizer to top portion of the rotary drum, making said fertilizer fall down and pass through tray and distribute to form uniform fertilizer granule curtain, spraying liquid urea from nozzle and uniformly coating fertilizer granules with liquid urea.

Description

1. Technical field [0001] The invention relates to a manufacturing method of a compound fertilizer, more specifically to a manufacturing method for increasing the nitrogen content of a granule compound fertilizer by adopting a urea solution curtain coating method. 2. Background technology [0002] The production of compound fertilizer mainly includes slurry method, pellet method, melt method, extrusion method and blending method. Drum granulation in the agglomeration method is widely used by large-scale compound fertilizer manufacturers due to its advantages of high granulation possibility, good product quality, less dust, and large production capacity. [0003] In the prior art, the drum urea granulation technology adopted by Girdler Inc. of the United States is to spray molten urea on the rolling bed of solid particles in the drum, and the particles are coated with a thin layer of liquid due to the rolling action. And gradually generate hard spherical particles, after coo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05C5/04C05G1/00C05G5/00
Inventor 邹鸿昌潘振玉陈靖宇陶谋鑫徐从龄
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap