Method for producing Sm-Fe-N permanent magnet alloy powder by reduction diffusion

A technology of permanent magnetic alloy and diffusion method, which is applied in the field of magnetic materials, can solve the problems of high melting point, achieve high-performance anisotropy, reduce volatilization loss, and improve the magnetic properties of powder

Inactive Publication Date: 2003-06-18
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But Sm 2 o 3 The melting point of Sm is higher, reaching 2325°C, while the vapor press

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The raw material adopts SmCl 3 , Fe powder (500 orders), calculate the chemical dose of each reactant required by formula (1), SmCl 3 The amount added is 103% of the stoichiometric dose, the metal Ca particle size is 3mm, and the added amount exceeds the stoichiometric dose by 15%, SmCl 3 After vacuum dehydration at 360°C. The reduction diffusion reaction was carried out under the protection of argon, and kept at 820°C for 2 hours. The reaction block was naturally pulverized in water, and the powder was filtered out and dried in vacuum. Alloy powder in NH with a pressure of 0.1Mpa 4 Treated at 450°C for 1 hour in the atmosphere, the magnetic properties of the prepared Sm-Fe-N alloy powder are: Br=9.8kGs, M Hc=8kOe, (BH)m=18MGOe.

Embodiment 2

[0021] The raw material adopts SmCl 3 , Fe powder (500 mesh) and Co powder (500 mesh), according to formula (1) calculate the stoichiometric dose of each reactant required, SmCl 3 The amount added is 105% of the stoichiometric amount, Co replaces 5% of the amount of Fe powder, the particle size of metal Ca is 3mm, and the added amount is 120% of the stoichiometric amount. SmCl 3 After vacuum dehydration at 360°C. The reduction diffusion reaction was carried out under the protection of argon, and kept at 850°C for 2 hours. The reaction block was naturally powdered in water, and the powder was filtered out and dried in vacuum. Alloy powder in NH with a pressure of 0.2Mpa 4 and H 2 (7.5:2.5) in a mixed atmosphere of 450 ° C for 1 hour, the magnetic properties of the prepared Sm-Fe-N alloy powder are: Br=11.2kGs, M Hc = 9.8kOe, (BH)m = 26MGOe.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

A process for preparing permanent-magnet Sm-Fe-N alloy powder by reduction-diffusion method includes such steps as choosing and pretreating raw materials, proportioning, mixing, thermal reducing and diffusion alloying at 760-860 deg.C by use of Ca and CaH2 as reducer to obtain Sm-Fe alloy and by-products, chemical separating, dewatering Sm-Fe alloy powder, nitrizing, and preparing anisotropic Sm-Fe-N magnet. Its advantages are low reaction temp, less loss of Sm and high performance.

Description

Technical field: [0001] The invention belongs to the field of magnetic materials, and in particular provides a method for manufacturing Sm-Fe-N permanent magnetic alloy powder. Background technique: [0002] Sm-Fe-N series alloy is a kind of rare earth permanent magnet material with excellent performance. In terms of basic magnetic properties, its saturation magnetization is equivalent to that of R-Fe-B system, and the anisotropy field and Curie temperature ratio R- Fe-B should be high. Since Sm-Fe-N will decompose when it is higher than 600°C, it is mainly used to manufacture bonded magnets, and the magnetic properties of bonded magnets mainly depend on the magnetic properties of Sm-Fe-N magnetic powder. At present, the preparation methods of Sm-Fe-N magnetic powder include ingot mechanical crushing method, also known as conventional method (IEEE.Trans.Mag.1993(29):2815); HDDR method (Physical Statuas Solidi A 1995(147):229); Rapid quenching method (J.Appl.Phys.1991.70(6)...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/20
Inventor 孙光飞陈菊芳
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap