Alite-barium calcium sulfur aluminate cement

A technology of barium calcium sulfoaluminate and tricalcium aluminate, which is applied in the field of cement materials, can solve the problems of high cost and unsuitability for mass production, and achieve the effects of accelerating hardening speed, saving limestone resources, and reducing shrinkage

Inactive Publication Date: 2004-07-21
UNIV OF JINAN
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main mineral of this kind of cement is mainly barium-containing sulfoaluminate, the proportion is 40-80%, and the main raw material is barite, etc., which has high cost and is suitable for special construction projects. Mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alite-barium calcium sulfur aluminate cement
  • Alite-barium calcium sulfur aluminate cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0035] The specific examples of Alite-barium calcium sulfoaluminate cement of the present invention are shown in Table 1, Table 2 and Table 3.

[0036] Table 1 Raw material ratio (for chemical reagents) %

[0037] Numbering

[0038] Prepare the raw meal according to the above six ingredients, and add a small amount of fluorite at the same time, according to CaF 2 Calculated as 0.6 to 1.2%. The chemical composition of the raw meal is shown in Table 2

[0039] Table 2 Chemical composition of cement raw meal %

[0040] Numbering

[0041] In the laboratory, the above clinker is fired in a silicon-molybdenum rod electric furnace, and the firing temperature is 1360°C-1380°C. The physical properties of cement are listed in Table 3.

[0042]

[0043] The 3# clinker was analyzed by XRD, as shown in Figure 1. It can be seen that in the alite-barium calcium sulfoaluminate cement clinker mineral system, a certain amount of alite and barium calcium sulf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

An Alinty-barium calcium thioaluminate cement contains barium calcium thioaluminate (3-38 wt.%), tricalcium aluminate (3-20), tricalcium silicate (30-60), dicalcium silicate (15-40), and ferroaluminate (3-20). Its advantages are low burning temp, high early strength and hardening speed, and low cost.

Description

(1) Technical field [0001] The invention belongs to the technical field of cement materials, in particular to an alite-barium calcium sulfoaluminate cement compounded with barium calcium sulfoaluminate mineral and alite mineral. (2) Background technology [0002] At present, Portland cement used in large quantities has some shortcomings and deficiencies, mainly manifested in high firing temperature (1450°C), low early strength and long setting time, resulting in high energy consumption for cement manufacturing and increased production costs. It has a certain influence on the construction speed and construction quality. Therefore, how to further reduce the firing temperature of Portland cement and improve its early performance is a key problem in the field of cement technology. [0003] For example, the Chinese patent "barium-containing sulfoaluminate cement" published on September 13, 1989 with the publication number CN1035486A is a fast-hardening and early-strength cement ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/00C04B7/345
CPCY02P40/10
Inventor 程新芦令超常钧刘福田于京华岳云龙王来国陈亚明
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com