Constant temperature curing high-bearing and anti-adhering wear resistant lubricating paint
A room temperature curing, high load-bearing technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of high raw material cost, narrow application range of coating film thickness, easy to scratch, etc., and achieve the effect of simple curing process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0037] Example 1:
[0038] Polyurethane 100g
[0039] PTFE wax 27g
[0040] Acetone 157g
[0041] Xylene 75 g
[0042] Cyclohexanone 43g
[0043] Additives: melamine cyanurate complex 13g
[0044] Weigh the above-mentioned materials, stir them evenly, and disperse in the ultrasonic wave. Use a spray gun to spray on the surface of the workpiece that has been dewatered, degreasing, decontaminated, and derusted under nitrogen at 0.2-0.4MPa. The wear-resistant life is 3000m at room temperature. / μm, the friction coefficient is 0.16-0.17; the wear resistance life is 2600m / μm at 120°C, and the friction coefficient is 0.17-0.18; the wear resistance life is 2300m / μm at 150°C, and the friction coefficient is 0.18-0.19.
Example Embodiment
[0045] Example 2:
[0046] Polyurethane 100g
[0047] Tetrafluoro wax 33 g
[0048] Acetone 172g
[0049]Xylene 86 g
[0050] Cyclohexanone 43g
[0051] Assistant: Antimony trioxide 16 grams
[0052] Weigh the above-mentioned materials, stir them evenly, and disperse in the ultrasonic wave. Use a spray gun to spray on the surface of the workpiece that has been dewatered, degreasing, decontamination, and derusting under 0.2-0.4MPa nitrogen. At room temperature, the load is 680 Newtons. The speed is 2.0m / s, the wear life is 2200m / μm, and the friction coefficient is 0.13-0.15; at room temperature, the load is 320 Newtons, the speed is 2.5m / s, and the coating is sprayed on the micro-arc oxidation layer of the aluminum substrate. The wear life is 2600m / μm., and the friction coefficient is 0.15-0.18.
Example Embodiment
[0053] Example 3:
[0054] Polyurethane 100g
[0055] Tetrafluoro wax 47g
[0056] Acetone 146g
[0057] Xylene 63 g
[0058] Cyclohexanone 37 g
[0059] Assistant: melamine cyanurate complex 6.5g
[0060] Antimony trioxide 10.6
[0061] Weigh the above-mentioned materials, stir them evenly, and disperse in the ultrasonic wave. Use a spray gun to spray on the surface of the workpiece that has been dewatered, deoiled, decontaminated, and derusted under 0.2-0.4MPa nitrogen. It is wear-resistant under the action of room temperature water medium The service life is 2170m / μm, and the friction coefficient is 0.06-0.10; the wear resistance life is 2230m / μm. at 180°C, and the friction coefficient is 0.17-0.18.
PUM
Property | Measurement | Unit |
---|---|---|
Wear life | aaaaa | aaaaa |
Wear life | aaaaa | aaaaa |
Wear life | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap