Environment protecting dry brick and its production process

A manufacturing method and technology of clear-water bricks, which are applied to clay products, other household appliances, household appliances, etc., can solve the problems of low compressive strength, and achieve the effect of increasing the dosage, expanding the dosage, and improving the artistic content.

Inactive Publication Date: 2005-07-13
WUHAN UNIV OF TECH +1
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its fly ash and red mud are the main raw materials, but due to extrusion molding, the firing temperature is only about 1050 ° C, so its compressive strength is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of manufacture method of the artistic environment-friendly clean water brick with blue marble decoration, the steps are as follows:

[0024] 1) Batching: a. The batching of brick is made of 85wt% base material and 15wt% cobalt blue colored blank; The solubilizing additive is diopside; c. cobalt blue coloring blank is configured by mixing base material and cobalt blue material, wherein the addition of cobalt blue material accounts for 20% of the total weight of cobalt blue coloring blank, and the base material The formula is: 80wt% alumina red mud, 18wt% shale, 2wt% solubilizing additive, the solubilizing additive is diopside, and the formula of the base material is the same as that of the base material;

[0025] 2) Grinding and mixing: Put the raw materials of each component of the base material into a ball mill to grind, the grinding time is 12 hours, the ingredients are mixed, and then sieved to 120 mesh for later use;

[0026] 3) Granulation: the base materia...

Embodiment 2

[0033] A method for manufacturing an artistic environment-friendly clear water brick with a rainbow ribbon, the steps are as follows:

[0034] Batching: a. The batching of the brick is composed of 85wt% base material and 15wt% colored blank; b. The base material formula is: 80wt% of alumina red mud, 14wt% of shale, 6wt% of solubilizing additive, the described solubilizing additive It is silicon pyroxene; c. The colored blank is prepared by mixing base material, manganese red material and chrome green material, wherein the addition of manganese red material accounts for 4% of the total weight of the colored blank, and the chrome green material accounts for 4% of the total weight of the colored blank. 8%, the formula of the primer is: 80wt% of alumina red mud, 14wt% of shale, 6wt% of solubilizing additive, the solubilizing additive is silica pyroxene, and the formula of the primer is the same as that of the base material;

[0035] 2) Grinding and mixing: Put the raw materials of...

Embodiment 3

[0043] A kind of manufacture method of antique artistic type environment-friendly clear water brick, the steps are as follows:

[0044]1) Batching: a. The batching of brick is made of 90wt% base material and 10wt% colored blank; b. base material formula is: alumina red mud 65wt%, shale 30wt%, solubilization additive 5wt%, described The solvent additive is silicon pyroxene; c. The colored blank is configured by mixing the base material, cobalt blue material and chrome green material, wherein the addition of cobalt blue material accounts for 6% of the total weight of the colored blank, and the addition of chrome green material The amount accounts for 3% of the total weight of the colored blank, and the formula of the primer is: 65wt% of alumina red mud, 30wt% of shale, 5wt% of the solubilizing additive, and the described solubilizing additive is silicon pyroxene. same base material;

[0045] 2) Grinding and mixing: Put the raw materials of each component of the base material in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The present invention relates to wall material and its production process. The environment protecting dry wall brick is prepared with base material in 80-90 wt% and colorizing material 10-20 wt%. The base material includes red alumina clay 60-80 wt%, shale 10-30 wt% and flux additive diopside or wollastonite 2-10 wt%; and the colorizing material consists of bottom material and pigment, with the bottom material having the same recipe as the base material and the pigment accounting for 5-20 wt% of the colorizing material. The production process includes forming the colorizing material and the base material in two times into mold with grains, drying, glazing and baking. The produced environment protecting dry wall brick is used in laying building wall without needing decorating and results in excellent outer wall decoration effect.

Description

technical field [0001] The invention relates to a wall material and a manufacturing method thereof, in particular to a clear water brick made from solid waste and a manufacturing method thereof. Background technique [0002] Clear water brick is a kind of sintered brick. For example, in ancient my country, a large number of red bricks and blue bricks were directly built into the wall without other external decorations in some ancient buildings. This ancient clear water brick wall is natural and simple, but not Durable, after a long time, the surface will peel off and corrode, which is very unsightly. With the progress of the times, the exposed brick walls are gradually replaced by cement mortar (sometimes with exterior wall paint) and ceramic exterior wall tiles. First, it plays a protective role and is more durable; second, it plays a decorative role. It is more beautiful; however, this type of wall is easy to stain, discolor or fall off, and it is time-consuming and labori...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/02C04B33/13
Inventor 吴建锋刘云鹏徐晓虹贾元平潘长学卢家喜
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com