Injectiong coagulation shaping technology of high performance graphite product

A graphite product, injection molding technology, applied in clay products, applications, household appliances, etc., can solve the problems of high energy consumption in the molding process, inability to form at one time, complex shapes, etc., to achieve isotropy, improve reliability, reduce The effect of production costs

Inactive Publication Date: 2005-08-24
OCEAN UNIV OF CHINA
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a high-performance graphite product injection molding process, which can overcome the shortcomings of the existing graphite product forming process, such as high energy consumption, long cycle, and inability to form complex shapes at one time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Injectiong coagulation shaping technology of high performance graphite product
  • Injectiong coagulation shaping technology of high performance graphite product
  • Injectiong coagulation shaping technology of high performance graphite product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] (1) Preparation of graphite carbon paste and related performance tests.

[0016] Weigh 150 grams of organic monomer acrylamide, 25 grams of crosslinking agent N,N'-methylenebisacrylamide, and 20 grams of dispersant sodium dodecylsulfonate, add it to distilled water, stir at room temperature, and make the above The reagents were fully dissolved and made into a 1000 ml solution, and the pH was adjusted to 11.0 with concentrated ammonia water; Ball milling at the speed of revolution per minute for a total of 24 hours to obtain graphite carbon slurry.

[0017] The carbon source in the present invention is natural graphite or synthetic graphite; the content of graphite in the carbon slurry is 20vol%-50vol%. The organic monomer is an organic compound containing vinyl, allyl, acrylate, acrylamide or acrylic functional groups, and the crosslinking agent is N, N'-methylenebisacrylamide; the sum of the content of the organic monomer and the crosslinking agent It is 5wt%-20wt% o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A moulding process for preparing high-performance graphite product includes such steps as proportionally mixing graphite, organic monomer, cross-linking agent, disperser and water, regulating pH value, mixing it with trigger, stirring, loading in mould, solidifying, demoulding and sintering.

Description

technical field [0001] The invention relates to a gel injection molding process of graphite products, which belongs to the field of inorganic non-metallic materials. Mainly used in refractory materials, wear-resistant materials, lubricating materials, electric carbon materials, coatings and other fields. Background technique [0002] The preparation of high-performance carbon and graphite materials is a long process with high energy consumption. The traditional method of preparing carbon or graphite composite materials from organic precursors requires several carbonization, graphitization, and densification under high pressure conditions. Generally, it takes 5 cycles, which is time-consuming and energy-consuming. Compared with hot pressing, it can reduce the cost and shorten the preparation time. However, the shape of the obtained product is limited by the hot pressing mold and can only be sheet or columnar. Therefore, the product still needs further processing, thus prolon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/28C04B35/52
Inventor 黄翔马峻峰戴金辉朱志斌吴平伟胡应模王洪芬陈海燕
Owner OCEAN UNIV OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com