Heat insulated anticorrosive coating for coiled material, and fabricating method

An anti-corrosion coil and coil coating technology, applied in anti-corrosion coatings, polyester coatings, coatings, etc., can solve the problem of no thermal insulation and anti-corrosion coil coatings, and achieve economic and social benefits, cost savings, excellent The effect of corrosion resistance

Inactive Publication Date: 2006-04-19
广东创想现代产业科技有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As mentioned above, since the problem of rapid drying and curing of heat-insulating coatings at process temperatures has not yet been solved, there is no heat-insulating and anti-corrosion coil coating suitable for the application of drying tunnel furnaces in assembly lines.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described in detail below in conjunction with specific examples.

[0024] As shown in Table-2, the ratio of raw materials for two kinds of heat-insulating and anti-corrosion coil coatings:

[0025]

process

Raw material name

Example, kg

example 1

Example 2

first step

pre-dissolved

150# solvent oil

Dibasic acid dimethyl ester

XD8560 polyester resin

SN8000 amino resin

10.0

4.0

50.0

8.0

9.0

5.0

50.0

8.0

second step

mix

dispersed

grinding

R828 titanium dioxide

800 mesh light aluminum silicate

nano-SiO X 〔1〕 / TiO X 〔2〕

TM-501 coupling agent

TM-108 hyperdispersant

TM-118 anti-settling agent

F-881C Thixotropic Agent

12.0

3.0

3.5 1〕

0.5

1.0

1.5

0.7

11.0

5.0

4.0 〔2〕

0.5

1.0

1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A paint for the coiled insulating and anticorrosion material is prepared from special polyester resin, high etherified cross-linking resin and pigment, functional insulating filler, special chemical assistant and solvent through proportional mixing, dispersing, grinding, adding insulating filler, etc. Its advantages are no poison and pollution, high flame-retarding and insulating effect, and high resistance to ageing and corrosion.

Description

technical field [0001] The invention relates to a heat-insulating and anti-corrosion coil coating and a manufacturing method thereof, belonging to the technical field of chemical compositions. Background technique [0002] At present, the galvanized steel sheet coils and colored steel sheet coils on the market do not have the function of heat insulation. If galvanized tiles and color steel tiles pressed by such steel plates are used for roof covering, the indoor temperature will rise to 40-50°C in hot summer, which is scorching hot and unbearably hot. In order to solve this problem, in recent years, someone has developed a heat-insulating coating for building roofs (cement surfaces, colored tile surfaces) and exterior walls. However, these coatings all belong to the self-drying repair paint category, and are not suitable for the coating process of cold-rolled strips operated by automated production lines. [0003] The color steel plate coated with ordinary coil coating abs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D5/08
Inventor 张驰
Owner 广东创想现代产业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap