Technology of producing Ti micro alloyed high weather resistant steel plate using thin plate blank continuous casting continuous milling process

A thin slab continuous casting and microalloying technology, used in metal rolling and other directions

Inactive Publication Date: 2006-06-14
GUANGZHOU PEARL RIVER STEEL & IRON
View PDF0 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] The new composition design and process of producing high-strength weather-resistant steel plates with a yield strength of 450 MPa or more by using the thin slab continuous casting and rolling process has not been reported at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention applies the process of thin slab continuous casting and rolling to produce Ti microalloyed high-strength weather-resistant steel plate. According to the characteristics of thin slab continuous casting and rolling process and the metallurgical composition of molten steel, electric furnace or converter is used for smelting, refining, thin slab continuous casting, casting After the slab is solidified, it directly enters the process flow of roller hearth heating or soaking furnace, hot rolling, laminar cooling, and coiling. The temperature of the thin slab entering the furnace is 900-1100°C, the temperature of exiting the furnace is 1050-1180°C, and the temperature of final rolling is 850-850°C. 910℃, after laminar cooling, the coiling temperature is 550~650℃, the metallurgical composition range of molten steel is: C: 0.04~0.07wt%; Si: 0.3~0.5wt%; Mn: 0.4~1.2wt%; P: 0.075 ~0.10wt%; S: ≤0.005wt%; Cu: 0.20~0.40wt%; Ni: 0.15~0.35wt%; Ti: 0.02~0.15wt%; Cr: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

A conticasting and tandem rolling technology for manufacturing the high-strength and-weatherability Ti-microalloyed steel plate includes such steps as smelting, refining, conticasting, solidifying, heating, hot rolling, laminar flow cooling and coiling. Its advantages are high strength, high shaping performance, high weatherability and high weldability.

Description

technical field [0001] The invention relates to a production process of a high-strength weather-resistant steel plate. Background technique [0002] High-strength weather-resistant steel plates are important materials for containers, railway carriages, and urban subway carriages. With the economic development of our country, the logistics industry is growing rapidly. High-strength weathering steel plays an important role in reducing weight, increasing speed, increasing freight volume, prolonging the service life of equipment and reducing logistics costs. High-strength weathering steel refers to σ s ≥450MPa weathering steel, this type of steel is mainly used in the manufacture of special containers, bridges and high-speed train carriages. Since high-strength weathering steel requires high corrosion resistance and high strength level, good formability and welding performance, it requires a high level of metallurgical process and equipment control. [0003] (1) Overview of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/46C22C38/50
Inventor 毛新平康永林李烈军林振源周建谢利群陈学文许传棻刘义军邹安华庄汉洲王湘飞张武彬霍向东孙新军
Owner GUANGZHOU PEARL RIVER STEEL & IRON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap