Plasticizer for ceramet production

A technology of cermets and molding agents, which is applied in the field of molding agents produced by powder metallurgy, and can solve the problems of low compaction strength, high pressing pressure, and easy dirt.

Inactive Publication Date: 2006-07-19
ZHUZHOU CEMENTED CARBIDE CUTTING TOOLS CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of rubber-based molding agents is good molding performance, but the disadvantage is that the residual carbon is high and difficult to control, inconvenient to use, and pollutes the vacuum system
The advantage of paraffin wax is that there is little residue, but the disadvantage is that the molding performance is not ideal, the compact strength is low, it is easy to dirty, it is inconvenient t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plasticizer for ceramet production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: put into the autoclave together with the polyvinylpyridine of 20% by weight, the polyethylene glycol of 38%, the stearic acid of 2% and the dehydrated alcohol of 40%, be heated to about 50 ℃, and Stirring and blending to form a uniform solution, that is, to obtain the forming agent of the present invention, which is used for the production of ultrafine Ti(CN)-based cermets.

Embodiment 2

[0014] Embodiment 2: be that 40% polyvinylpyridine, 20% polyethylene glycol, 10% stearic acid and 40% dehydrated alcohol are put into autoclave together by weight percentage, be heated to about 50 ℃, and Stir and blend to form a uniform solution, that is, to obtain the forming agent of the present invention, which is suitable for the production of complex-shaped cermet products.

Embodiment 3

[0015] Embodiment 3: be that 24% polyvinylpyridine, 10% polyethylene glycol, 6% stearic acid and 60% dehydrated alcohol are put into autoclave together by weight percentage, are heated to about 50 ℃, and Stir and blend to form a homogeneous solution, that is, to obtain the molding agent of the present invention, which is suitable for the production of micron-based cermets.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a plasticizer for ceramic metal production, which is prepared from 5-40% of polyvinylpyridine, 10-38% of polyethylene glycol, 2-10% of stearic acid, and 40-80% of anhydrous alcohol through heating, agitating and blending, and forming homogeneous solution. The invention can be applied into the production of cemented carbide and ceramics.

Description

technical field [0001] The invention relates to a molding agent for powder metallurgy production, especially a molding agent suitable for cermet production. Background technique [0002] In the production process of cermets, a certain amount of molding agent must be added in order to make powder compacted into products of various shapes. The molding agents currently used mainly include rubber: butadiene rubber, butadiene rubber, styrene-butadiene-styrene block polymer (SBS), styrene-isoprene-styrene (SIS), etc.; Paraffins; polyethylene glycol (PEG) water-soluble polymers. The advantages of rubber-based molding agents are good molding performance, but the disadvantages are that the residual carbon is high and difficult to control, inconvenient to use, and pollutes the vacuum system. The advantage of paraffin wax is that there is little residue, but the disadvantage is that the molding performance is not ideal, the compact strength is low, it is easy to dirty, it is inconven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00C04B35/632
Inventor 周书助肖哲王社权
Owner ZHUZHOU CEMENTED CARBIDE CUTTING TOOLS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap