Aqueous environmental protection ultration expansion type steel structure fireproof paint and its preparation method

A technology for fire-resistant coatings and steel structures, applied in fire-resistant coatings, coatings, liquid injection devices, etc., can solve the problems of large dosage, cracking of the expansion layer, affecting the adhesion of coatings, etc., and achieves good decorative performance, low dosage, and cost. low effect

Inactive Publication Date: 2006-08-30
北京首纳东方科技有限公司
View PDF4 Cites 54 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, Chinese patent CN 1394923A discloses a water-based thin intumescent steel structure fireproof coating, which also uses expandable graphite as an expansion reinforcing material, but the required amount is relatively large, such as 4-10%, which will affect the adhesion of the coating. Excessive internal stress may be generated to crack the expansion layer; in addition, when the fireproof coating is 3 mm thick, its fire resistance limit can only reach 75 minutes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous environmental protection ultration expansion type steel structure fireproof paint and its preparation method
  • Aqueous environmental protection ultration expansion type steel structure fireproof paint and its preparation method
  • Aqueous environmental protection ultration expansion type steel structure fireproof paint and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] According to the components listed below and content (weight percentage), prepare steel structure fireproof coating of the present invention:

[0080] water 17.35

[0081] Acrylic Emulsion 14.2

[0082] Chlorine partial emulsion 14.2

[0083] Expandable graphite 0.2

[0084] Ammonium polyphosphate with degree of polymerization n>1000 21

[0085] Pentaerythritol 8.5

[0086] Melamine 12.7

[0087] Titanium dioxide 8

[0088] Talc powder 2

[0089] 1,2-propanediol 0.17

[0090] 3-Methacryloxypropenetrimethoxysilane 0.56

[0091] 1,2-Benzisothiazolin-3-one 0.07

[0092] Polymethyltriethoxysilane 0.05

[0093] Organic Bentonite 1.

[0094] Add the above-mentioned additives into the dispersion tank, then add pentaerythritol into the water and raise the temperature to about 80°C. After the pentaerythritol dissolves, pour it into the dispersion tank, and immediately add the above-mentioned solid flame-retardant components and fillers, and then the The line speed is...

Embodiment 2

[0098] According to the components listed below and content (weight percentage), prepare steel structure fireproof coating of the present invention:

[0099] water 13.35

[0100] Acrylic emulsion 14.7

[0101] Chlorine partial emulsion 14.7

[0102] Expandable graphite 0.2

[0103] Ammonium polyphosphate with degree of polymerization n>1000 22

[0104] Pentaerythritol 9.5

[0105] Melamine 13.7

[0106] Titanium dioxide 8

[0107] Talc powder 2

[0108]1,2-propanediol 0.17

[0109] 3-Methacryloxypropenetrimethoxysilane 0.56

[0110] 1,2-Benzisothiazolin-3-one 0.07

[0111] Polymethyltriethoxysilane 0.05

[0112] Organic Bentonite 1.

[0113] Add the additives to the dispersion tank, then mix the pulverized and sieved pentaerythritol with solid components such as melamine, titanium dioxide, ammonium polyphosphate, and expandable graphite, and add it to the dispersion tank and stir to make it evenly mixed, and finally add Stir the organic bentonite for another 10 min...

Embodiment 3

[0116] According to the components listed below and content (weight percentage), prepare steel structure fireproof coating of the present invention:

[0117] water 20.35

[0118] Acrylic Emulsion 14.2

[0119] Chlorine partial emulsion 14.2

[0120] Expandable graphite 0.2

[0121] Ammonium polyphosphate with degree of polymerization n>1000 19

[0122] Pentaerythritol 7.5

[0123] Melamine 11.7

[0124] Titanium dioxide 8

[0125] Talc powder 2

[0126] 1,2-propanediol 0.17

[0127] 3-Methacryloxypropenetrimethoxysilane 0.56

[0128] 1,2-Benzisothiazolin-3-one 0.07

[0129] Polymethyltriethoxysilane 0.05

[0130] Hydroxyethyl Cellulose 1

[0131] Organic bentonite 1

[0132] Add the above-mentioned additives into the dispersion tank, then add pentaerythritol into the water and raise the temperature to about 80°C. After the pentaerythritol dissolves, pour it into the dispersion tank, and immediately add the above-mentioned solid flame-retardant components and filler...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a water environment-protecting superthin expanded type steel structure fire-retardant coating. Said fire-retardant coating uses water as dispersion medium, uses flake expandable graphite as expansion reinforcing material, uses one or several kinds of emulsions of acrylic emulsion and others as film-forming material, and its expansion system adopts the ingredients of polyammonium phosphate, pentaerythritol and tripolycyanamide. Said invention also provides its preparation method and concrete steps.

Description

technical field [0001] The invention relates to a water-based environmentally friendly ultra-thin intumescent steel structure fireproof coating and a preparation method thereof. Specifically, the present invention relates to a water-based environmentally friendly ultra-thin intumescent steel structure fireproof coating prepared by using water as the dispersion medium, using emulsion as the base material, and using expandable graphite as the expansion reinforcing material, and according to its different solid content. different preparation methods. Background technique [0002] At present, the rapid economic and social development has promoted the continuous upgrading and replacement of building materials, resulting in an increasing number of large buildings, and the main load-bearing components of these large buildings mostly rely on strong and light steel, which endows the building with a wide, The style of lightness, simplicity and smoothness without losing stability will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02C09D5/18B05B7/14
Inventor 咸才军刘学军付若愚郭保文郭奋关延涛
Owner 北京首纳东方科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com