Preparation method of graft starch

A technology for grafting starch and starch, applied in the field of preparation of grafted starch, can solve the problems of high viscosity, unfavorable grafting reaction, high price of grafted starch, lower yield of grafted starch, etc., and achieves easy environmental pollution and large implementation. Value and socio-economic benefits, low-cost effects

Inactive Publication Date: 2006-11-29
ZHEJIANG UNIV OF TECH
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the grafted starch synthesized is generally prepared by suspension and emulsion graft polymerization of starch dispersed in water, but the product of this method is not conducive to grafting reaction due to the high viscosity of starch after gelatinization in water. In order to reduce the viscosity of the grafted reactant, it is convenient Stirring, generally the concentration of starch is very low, which will greatly reduce the yield of grafted starch, generate a large amount of waste water, consume a large amount of energy, and make the subsequent separation process difficult, resulting in expensive grafted starch and difficult Industrial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1: The effect of reaction temperature on grafting rate

[0036] Add 200 grams of corn starch, 400 grams of industrial ethanol, and 200 grams of deionized water to a 1000 ml four-necked reaction flask equipped with a reflux condenser, swell at 50°C for 30 minutes, heat up to the specified temperature, and add 1 gram of diphenyl peroxide dropwise Formyl (BPO) and 50 grams of styrene, drip in 2 hours, react at a constant temperature for 3 hours, filter, wash the product, and determine the grafting rate after drying. The grafting rate of starch at different temperatures is shown in Table 1:

[0037] Reaction temperature, ℃

Embodiment 2

[0038] Example 2: Effect of reaction time on grafting rate

[0039] Add 300 grams of sweet potato starch, 500 grams of edible ethanol, and 100 grams of deionized water to 1000 ml of four-necked reaction flask equipped with a reflux condenser, swell at 50°C for 30 minutes, heat up to 80°C, and add 10 grams of 20% mass concentration dropwise The solution of potassium persulfate and 100 grams of vinyl acetate, after 2 hours of dripping, constant temperature reaction for different time, filter, wash the product, after drying to determine the grafting rate, the starch grafting rate of different constant temperature reaction time is shown in Table 2:

[0040] Reaction time, h

Embodiment 3

[0041] Example 3: The effect of the amount of grafting monomer on the grafting rate

[0042] Add 250 grams of corn starch, 400 grams of medical ethanol, and 200 grams of de-distilled water into a 1000 ml four-necked reaction flask equipped with a reflux condenser, swell at 50°C for 30 minutes, heat up to 75°C, and add 7.5 grams of 20% mass concentration dropwise Ammonium persulfate aqueous solution and formula amount of methyl methacrylate (MMA), drip in 2 hours, react at constant temperature for 3 hours, filter, wash the product, and determine the grafting rate after drying, and the starch grafting rate for different amounts of grafting monomers as follows:

[0043] MMA, g

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A graft starch is prepared through proportionally adding starch, alcohol as disperser and water into reactor stirring, swelling, heating to 70-90 deg.C, dripping trigger and grafting monomer, stirring while reacting, cooling, filtering, washing, and drying.

Description

(1) Technical field [0001] The invention relates to a preparation method of grafted starch. (2) Background technology [0002] At present, synthetic grafted starches are generally prepared by the suspension and emulsion graft polymerization of starch dispersed in water. However, the product of this method is not conducive to the grafting reaction due to the high viscosity of the starch after gelatinization in water. In order to reduce the viscosity of the grafting reactant, it is convenient Stirring, the general starch concentration is very low, which will greatly reduce the yield of grafted starch, produce a lot of waste water, consume a lot of energy, and make the subsequent separation process difficult, resulting in expensive and difficult grafting starch. Industrial applications. (3) Contents of the invention [0003] In order to solve the above-mentioned shortcomings in the preparation of grafted starch in the prior art, the present invention provides a grafted starch with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F251/00
Inventor 邬润德童莜莉
Owner ZHEJIANG UNIV OF TECH