Porous polypropylene particle suspension solid phase graft-modification method

A technology of suspension grafting and solid phase grafting, which is applied in the field of porous polypropylene particle suspension solid phase grafting modification, can solve the problem of unsuitable monomers with large solubility, low grafting depth, reactants and The product is difficult to separate and other problems, and the effect of no pollution, simple process and improved mechanical properties is achieved.

Active Publication Date: 2006-12-27
BEIJING UNIV OF CHEM TECH
View PDF0 Cites 50 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] However, since this method uses pure water as the reaction medium, there are certain restrictions on grafted monomers, and it is not suitabl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous polypropylene particle suspension solid phase graft-modification method
  • Porous polypropylene particle suspension solid phase graft-modification method
  • Porous polypropylene particle suspension solid phase graft-modification method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Dissolve the initiator benzoyl peroxide in the acrylic acid monomer according to 0.5% of the mass of the monomer, and then soak the porous polypropylene (PP) particles with a porosity of 0.14-0.44 in the above-mentioned monomer / initiator solution for 30 Minutes, so that monomers and initiators are fully adsorbed into the pores of PP particles. Prepare sodium chloride brine with a concentration of 20%, put it in the reactor, turn on the stirring and heating device, and when the temperature reaches 85°C, put in PP particles soaked in monomer and initiator, react for 2 hours, and discharge , washed with distilled water and acetone to remove unreacted monomers and initiators, and then dried to obtain a graft-modified product.

Embodiment 2

[0032] Dissolve the initiator benzoyl peroxide in the methyl acrylate monomer according to 1% of the monomer mass, and then soak the porous polypropylene (PP) particles with a porosity of 0.14-0.44 in the above monomer / initiator solution For 20 minutes, the monomer and initiator are fully absorbed into the pores of PP particles. Prepare brine with a concentration of 35% sodium chloride, place it in the reactor, and turn on the stirring and heating device. When the temperature reaches 85°C, put PP particles soaked in monomers and initiators, react for 3 hours, discharge, wash with distilled water and acetone respectively, remove unreacted monomers and initiators, and then dry to obtain Graft modified products.

Embodiment 3

[0034] The initiator benzoyl peroxide is dissolved in acrylic acid and methyl acrylate monomer (mass ratio is 1:1) according to 1.5% of the monomer mass, and then the porous polypropylene (PP) particles with a porosity of 0.14-0.44 Soak in the above monomer / initiator solution for 30 minutes to fully absorb the monomer and initiator into the pores of PP particles. Prepare brine with a concentration of 25% sodium chloride, place it in the reactor, and turn on the stirring and heating device. When the temperature reaches 85°C, put PP particles soaked in monomers and initiators, react for 3 hours, discharge, wash with distilled water and acetone respectively, remove unreacted monomers and initiators, and then dry to obtain Graft modified products. The grafted product was injected into a specimen, and the notched impact strength (kJ / M 2 ) is 5.44, the tensile strength (Mpa) is 37.54, and the yield stress (Mpa) is 31.99.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Notched impact strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield stressaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for modifying grafting for porous polypropylene particle floating solid phase. The invention modifies floating solid phase grafting for polypropylene particle absorbed with monomer and initiator in salt solution, to increase grafting depth, reduce degradation and side reaction, and improve mechanics property for polypropylene. The modified product can also be used as compatible agent for PP and other polymer to increase material compatibility and then improve mechanics property.

Description

Technical field: [0001] The invention relates to a porous polypropylene particle suspension solid-phase graft modification method. Background technique: [0002] Among the five general-purpose plastics, polypropylene (PP) has a short development history, but it is the fastest growing one. Its output and production capacity are steadily increasing, with an annual growth rate of 8-12%. The United States, Western Europe and Japan The production capacity of other countries accounts for 2 / 3 of the world. However, the share of high value-added products is relatively small, which leads to their inability to meet the rapidly growing needs of the market, especially the plastic products industry. For this reason, the PP industry at home and abroad is actively adjusting the industrial structure, opening up new application fields, adding new high-performance varieties and grades, developing PP-based alloy materials, vigorously researching and developing PP modified products and technol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F255/02
Inventor 杨万泰罗伟孙玉凤何辰凤
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap