Method for polyolefin porous film mfg. method
A technology of microporous membrane and manufacturing method, applied in the direction of chemical instruments and methods, membrane technology, semi-permeable membrane separation, etc., to achieve the effects of reducing production costs, anti-acupuncture performance, and high strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1:
[0028] Manufacturing method of ultra-high molecular weight polyethylene microporous membrane
[0029] Material formula:
[0030] Ultra-high molecular weight polyethylene (UHMWPE) with a weight average molecular weight (Mw) of 2.5 million: 25 parts; Diisodecyl phthalate (DIDP): 70 parts; Polyisobutylene PIB: 5 parts;
[0031] processing methods:
[0032] (1) above-mentioned raw material is first carried out 95 ℃ of swelling and mixing treatment for 16 hours, and is prepared into uniform slurry; then by metering pump, the slurry is input into a parallel co-rotating twin-screw extruder for melting and kneading, and the temperature of each zone of the twin-screw is set to 170 ℃ , 180, 180, 180, 180, 180 ℃, the temperature of the melt gear pump is set to 180 ℃, the temperature of the die head is set to 180 ℃; the semi-finished product is cast film, and the thickness is controlled to 75-80 microns;
[0033] (2) Then use supercritical extraction on the semi-fin...
Example Embodiment
[0035] Example 2:
[0036] Manufacturing method of ultra-high molecular weight polyethylene microporous membrane
[0037] The extraction agent adopts refrigerant R125. The extraction agent is preheated by a 95°C preheater before entering the extraction kettle after pressurization. The heating temperature of the jacket jacket of the extraction kettle is set to 95°C, and the heated R125 extractant is pumped into the extraction kettle. After the pressure of the kettle is increased to 4MPa, close the extraction agent inlet stop valve and high-pressure pump, and continue to heat the jacket of the extraction kettle for 15-60 minutes, then reopen the outlet pressure reducing valve, the extraction agent inlet stop valve, and turn on the high-pressure pump for continuous flow supercritical extraction. 10-60min, the extraction operation pressure is controlled at 8MPa, and the extraction process temperature is 90°C; after the outlet pressure reducing valve of the extraction kettle, the m...
Example Embodiment
[0038] Example 3:
[0039] Manufacturing method of polypropylene microporous membrane
[0040] Material formula:
[0041] Polypropylene (PP 3271): 40 parts; Diisodecyl phthalate (DIDP): 55 parts; Polyisobutylene PIB: 5 parts;
[0042] processing methods:
[0043] (1) The above-mentioned raw materials are first mixed at 110°C for 1-2 hours to prepare a uniform slurry; then the slurry is input into a parallel co-rotating twin-screw extruder through a metering pump for melting and kneading, and the temperature of each zone of the twin-screw is set to 180, 220, 210, 210, 210, 210 °C, the temperature of the melt gear pump is set to 210 °C, and the temperature of the die head is set to 210 °C; the semi-finished product is cast film, and the thickness is controlled to 30-35 microns;
[0044] (2) Then use supercritical extraction on the semi-finished product, and use refrigerant R125 as the extractant. 2 The polypropylene non-woven fabric is compounded and put into a 260L high-pre...
PUM
Property | Measurement | Unit |
---|---|---|
Aperture | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap