Anti-glare optical film and process for preparing the same

an optical film and anti-glare technology, applied in the field of optical films, can solve the problems of deteriorating the visibility of an image displaying device including a liquid crystal displaying device, high cost of former non-reflecting treatment, and inability to be said, so as to reduce the whitening of a screen, prevent glare, and reduce the effect of whitening

Inactive Publication Date: 2008-06-05
SUMITOMO CHEM CO LTD
View PDF10 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0013]The present invention is made in view of the above circumstances, and an object thereof is to provide an anti-glare optical film which reduces whitening of a screen without deteriorating anti-glare property, and a process for preparing the same. Another object of the present invention is to provide an anti-glare optical film which is suitably used on the surface of various displays including a liquid crystal displaying device, is small in whitening of a screen, and exhibits high effect of preventing glare.
[0015]In this anti-glare optical film, it is advantageous that a reflectivity towards a direction shifted from a specular reflection angle by 20° is 0.001% or less. In addition, it is advantageous that a 45° reflection clarity measured using an optical comb having a width between a dark part and light part of 1.0 mm is 50% or less. Further, it is advantageous that a total value of transmittance clarity measured using four kind of optical combs having a width between a dark part and a light part of 0.125 mm, 0.5 mm, 1.5 mm and 2.0 mm is 200% or more. Further, it is advantageous that this glare preventing optical film has a haze of 10% or less.

Problems solved by technology

Visibility of an image displaying device including a liquid crystal displaying device is remarkably deteriorated when the outdoor daylight is reflected on its image displaying surface.
The cost of former non-reflecting treatment is high due to necessity of formation of a multilayered film having a uniform optical film thickness.
In addition, in an even a method of obtaining anti-glare surface having no filler by a method of transferring a shape using a mat-like shaping film, since a reflected light distribution depends on a shape of a shaping film as a template, it can not be said that this method is not necessarily sufficient to prevent whitening.
However, as a method of forming irregularities on a shaping film, only a method of coating a composition composed of a filler and a binder resin on a substrate film to transfer the shape of the filler is disclosed and, since distribution of a filler and, consequently, arrangement of irregularities becomes random, it is thought that sufficient prevention of whitening can not be performed.
However, according to these formulations, a proportion of a flat surface of an anti-glare surface is increased at the same time, causing clarity of an image of the reflected on outdoor daylight, and anti-glare property is deteriorated.
However, the previously known glare preventing-treated film has not necessarily sufficient effect of preventing the aforementioned whitening, and it can not be said that sufficient visibility is obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-glare optical film and process for preparing the same
  • Anti-glare optical film and process for preparing the same
  • Anti-glare optical film and process for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0098]A soda-lime glass having a thickness of 1.1 mm obtained from Nippon Sheet Glass Co., Ltd. was blast-treated with a mono disperse aluminum crystal “Sumicorundum AA-5” (average particle diameter: 5 μm) obtained from Sumitomo Chemical Co., Ltd. A blast pressure was 0.5 kg / cm2 (50 kPa), and a blast time was 120 seconds. Thus blast-treated glass was ultrasound-washed, dried, immersed in 10% by weight hydrofluoric acid at 40° C. for 1,200 seconds, sufficiently washed with pure water, and dried to prepare a template glass.

[0099]10 g of a urethaneacrylate ultraviolet curing resin “UA-1” obtained from Shin-Nakamura Chemical Co., Ltd., and 0.5 g of a photopolymerization initiator “Lucirin TPO” (chemical name: 2,4,6-trimethylbenzoyldiphenylphosphine oxide) obtained from BASF Corporation were dissolved in 10 g of ethyl acetate to prepare a coating solution. This coating solution was coated on one side of triacetylcellulose film having a thickness of 80 μm obtained from Fuji Photo Film Co....

example 2

[0103]According to the same manner as that of Example 1 except that a blast particle was changed to “Sumicorundum AA-18” (average particle diameter: 18 μm) obtained from Sumitomo Chemical Co., Ltd., a blast pressure was 0.4 kg / cm2 (40 kPa), and a blast time was 120 seconds, an anti-glare optical film was prepared. Results of optical property and visible assessment of the resulting film are shown in Table 1. It was found that this film also has sufficient anti-glare property and whitening preventing ability.

example 3

[0108]A borosilicate glass plate (trade name “Pyrex”; 5 cm square, 4 mm thickness; purchased by designating size and thickness) manufactured by Asahi Techno Glass Co., Ltd. was blast-treated using a zirconia bead (trade name “TZ-B53”, average particle diameter 53 μm, approximately monodisperse) manufactured by Tosoh Co., Ltd. An amount of a blast agent (zirconia bead) used was 100 ml, a blast pressure was 0.03 MPa, a distance from a blast nozzle to a glass plate was 40 cm, and a blast gun was fixed. Blast treatment was completed in about 5 minutes. A glass after blast treatment remained approximately transparent, but when observed with a reflection-type microscope manufactured by Keyence Corporation, it was confirmed that many fine cracks were produced on the surface at a depth of about 1 to 1.5 μm.

[0109]A glass after blast was immersed in an etching solution of weight ratio 5 / 1 / 1 / 10 of hydrogen fluoride (HF) / ammonium fluoride ((NH4)2 SO4) / sulfuric acid (H2SO4) / water at a temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
average particle diameteraaaaaaaaaa
average diameteraaaaaaaaaa
reflection clarityaaaaaaaaaa
Login to View More

Abstract

An anti-glare optical film which reduces in whitening of a screen without sacrificing anti-glare property, and a process for preparing the same. There is provided an anti-glare optical film has an irregular surface, wherein a ratio of areas of the surface having an inclination angle of 1° or less is 20% or less, a ratio of areas of the surface having an inclination angle of 5° or more is 20% or less, and a standard deviation of a height of the surface is 0.2 μm or less. There is also provided a process for preparing an anti-glare optical film.

Description

BACKGROUND OF THE INVENTION[0001]1. Field of the Invention[0002]The present invention relates to an optical film imparted property of preventing glare, which is used in a polarizing film of an image displaying device, and a process for preparing the same.[0003]2. Description of the Related Art[0004]Visibility of an image displaying device including a liquid crystal displaying device is remarkably deteriorated when the outdoor daylight is reflected on its image displaying surface. In utilities requiring high quality of image such as a television and a personal computer, utilities used in outdoor where the outdoor light is intense such as a video camera and a digital camera, and utilities which perform display utilizing the reflected light such as a reflecting-type liquid crystal displaying device such as a portable phone, the surface of a displaying device is generally treated for preventing the reflecting thereon. Reflecting on preventing treatment is roughly classified into non-ref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): G02B27/00G02B1/11G02B5/02G02F1/1335
CPCG02B5/0221G02F1/133502G02B5/0268G02B5/0236G02B1/11G02B5/30
Inventor NAMIOKA, MAKOTOKUWABARA, MASATO
Owner SUMITOMO CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com