Superhigh-strength cold rolling band steel with anti-tensile strength above 880Mpa and its production

A technology of 880mpa, cold-rolled strip steel, applied in the direction of manufacturing tools, heat treatment process control, furnaces, etc., can solve the problems of strength decrease, increase alloy element content, increase cost, etc. The effect of generation

Active Publication Date: 2008-11-05
BAOSHAN IRON & STEEL CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to avoid the strength decrease caused by the reduction of carbon content, this method inevitably needs to greatly increase the content of alloying elements, so the cost is very high, and the tendency of cold and brittle is obvious
[0011] In short, the above inventions involving ultra-high-strength steel plates greatly increase the cooling rate and reduce the amount of alloying elements added. The technical requirements for equipment are extremely high, the shape of the plate is difficult to control, and in the welding process, it is easy to occur due to insufficient hardenability. The resulting softening of the heat-affected zone of the weld causes the strength of the weld to be lower than that of the base metal, which is not conducive to the improvement of the overall strength of the welded member
Another invention is to reduce the carbon content and increase the content of alloy elements, which not only increases the cost, but also easily causes hardening and embrittlement of the welding zone, which is not conducive to welding performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0053] The following are specific descriptions of Examples 1-7 of the present invention.

[0054] The concrete chemical composition of example 1-7 is shown in Table 1:

[0055] The chemical composition performance of table 1 example 1-7, Wt%

[0056] make up

No

C

Si

mn

P

S

Al

Ti

Nb

N

B

1

0.16

0.4

2.0

0.01

0.005

0.02

0.05

0.015

0.0032

0.004

2

0.17

0.5

2.5

0.01

0.018

0.044

0.04

0.03

0.0037

0.0045

3

0.2

0.2

2.3

0.019

0.005

0.05

0.08

0.02

0.0031

0.006

4

0.14

1.0

1.94

0.011

0.008

0.051

0.06

0.04

0.004

0.005

5

0.24

1.2

1.5

0.012

0.006...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

High strength cold-strip steel whose tensile strength is over 880Mpa , its component is ( weight percentage): C:0.14-0.24%;Si:0.2-1.2%;Mn:1.5-2.5%;P:<0.02%; S:<0.02%;N:<=0.005%;Ti:0.03-0.1%;Nb:0-0.04%;B:0.002- 0.006%;Al:0.02-0.08%;the other is composed of Fe and other inevitable impurity. Its method is as following: Steel billet-> hot-rolling-> acid-washing-> cold rolling-> continuous annealing; its main manufacture technological parameter is as following: The anneal temperature is between750DEG C-850DEG C, heat preservation time is controlled to between 40s-150s; Air cooling speed is 30-60DEG C / s, cooling down to350-500DEG C; The hydrocooling temperature is below 200DEG C; The drawing-back temperature is 150-300DEG C, drawing-back time is 100-300s; the unknit rate is 0-0.8%.

Description

technical field [0001] The invention relates to an ultra-high-strength cold-rolled steel strip and a manufacturing method thereof, in particular to an ultra-high-strength cold-rolled steel strip with a tensile strength above 880Mpa and a manufacturing method thereof. Background technique [0002] In order to reduce weight and save energy, the automobile industry requires the steel plate to be thinned. At the same time, due to the requirements for safety, the requirements for the rigidity of the vehicle body are also continuously increasing. Ultra-high-strength steel is especially suitable for the manufacture of automotive safety parts that require high strength but low molding requirements. Therefore, ultra-high-strength steel plates (>800Mpa grade) have good application prospects in automobile manufacturing. At present, ultra-high-strength steels are manufactured by rapid cooling process to obtain a certain amount of martensite. However, ultra-high-strength steel requi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C21D9/52C21D11/00
Inventor 朱晓东
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products