Degradable radioactive biliary stent and method for producing the same

A technology of bile duct stent and degradable material, which is applied in the field of medical devices, can solve problems such as bile duct stent stenosis, achieve short irradiation distance, and inhibit bile duct intima hyperplasia and tumor growth

Active Publication Date: 2009-12-23
六安市济民医药科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main technical problem to be solved by the present invention is to overcome the defects of the existing biliary stents and provide a degradable radioactive biliary stent with a new structure, which not only solves the restenosis problem of the ordinary NiTi alloy wire braided biliary stent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Use NiTi alloy wire to braid the bile duct stent by hand or machine;

[0032] (2) Brush a layer of mixed solution of collagen+hydrochloric acid (acetic acid)+P-32, Pd-103 or I-125 on the surface of the bile duct stent manufactured above to form peritoneum, and then place it in a cross-linked Soaking under the agent;

[0033] (3) It can be prepared after freezing and drying;

[0034] (4) Sterilize with ethylene oxide gas before use.

Embodiment 2

[0036] (1) Use NiTi alloy wire to braid the bile duct stent by hand or machine;

[0037] (2) Brush a layer of gelatin+water+P-32, Pd-103 or I-125 on the surface of the bile duct stent manufactured above to form a peritoneum, and then soak it under a cross-linking agent;

[0038] (3) It can be prepared after freezing and drying;

[0039] (4) Sterilize with ethylene oxide gas before use.

Embodiment 3

[0041] (1) Use NiTi alloy wire to braid the bile duct stent by hand or machine;

[0042] (2) Brush the mixed solution of one layer of chitosan+acetic acid+P-32, Pd-103 or I-125 on the surface of the bile duct stent manufactured above to form the peritoneum, and then place it in a cross-linking agent Soak under;

[0043] (3) It can be prepared after freezing and drying;

[0044] (4) Sterilize with ethylene oxide gas before use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a degradable radioactive bile duct stent for treating tumors and a manufacturing method thereof. The manufacturing method of the degradable radioactive biliary stent comprises the following steps: (1) using NiTi alloy wire to weave the biliary stent by hand or by machine; (3) It can be prepared after freezing and drying; (4) It needs to be sterilized with ethylene oxide gas before use. The invention is used for treating and inhibiting bile duct intima hyperplasia and tumor growth without causing damage to normal tissues, and its carrier collagen, gelatin or chitosan can complete the degradation process while performing internal radiation in the body, and finally participate in the metabolism of the human body and be excreted.

Description

technical field [0001] The invention relates to a medical device, more specifically to a degradable radiated bile duct stent for treating tumors and a manufacturing method thereof. Background technique [0002] In 1985, Carrasco invented the first metal expansion stent for bile duct (AJR Am J Roentgenol. 1985; 145(6): 1279-1281), which achieved relatively good therapeutic effect. Our country also gradually introduced this technology in the 1990s. Common metal expansion stents are used in bile duct drainage with less trauma, and a larger-diameter stent can be implanted with a smaller-diameter delivery tube. The case fatality rate is low. After being placed in the narrowed bile duct, it can expand to the original diameter at human body temperature, and produce continuous expansion force on the narrow tube wall, so as to maintain the stability of ordinary metal expansion stents and not easily shift. [0003] The bile duct stent braided by ordinary NiTi alloy wire is a good met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L31/14A61L31/16A61L31/10A61L31/02
Inventor 沈阳
Owner 六安市济民医药科技有限公司