Decorating plate brick producing process

A production process and technology for slab tiles, which are applied in the field of production technology of decorative slab tiles made of glass, can solve the problems of easy-wearing background color, uneven surface and high cost, and achieve a strong sense of three-dimensional layering, good transparency and tightness. good effect

Inactive Publication Date: 2007-08-08
潘文建
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polished tiles have the following disadvantages: the luminosity is unstable and uneven, and the color and luminosity of different batches of polished tiles are difficult to be the same; the anti-pollution ability is poor
Rustic bricks have the following disadvantages: high water absorption, rough surface, difficult to clean
The disadvantages of glazed tiles are: insufficient three-dimensional layering, easy to wear the background color, easy to appear pores on the surface, and cracks will appear when the temperature difference is large. The biggest problem is that the radioactivity of ceramic tiles should be treated to the extent that it will not affect human health. The process is complicated and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Edge grinding, grinding, polishing, cleaning, and pressing of protective film on glass bricks;

[0020] (2) Spray one deck of epoxy resin varnish uniformly on one surface of the glass brick;

[0021] (3) Evenly spread a layer of laser powder on the upper layer of the epoxy resin varnish, sweep and press on the laser powder with a row sweep, so that the laser powder is evenly attached to the glass brick, and stand until the epoxy varnish is dry;

[0022] (4) Spray the primer on the upper layer of the laser powder sheet, then bake at 150°C for 30 minutes, and cool;

[0023] (5) Use plastic printing to print the base screen paint on the base paint, and wait for it to dry or dry to obtain decorative tiles.

Embodiment 2

[0025] (1) Edge grinding, grinding, polishing, cleaning, and pressing of protective film on glass bricks;

[0026] (2) Use a plastic screen to print the pattern of the laser powder paste on the glass brick, bake at a temperature of 150°C for 45 minutes, and cool;

[0027] (3) Spray a layer of epoxy resin varnish evenly on one surface of the glass brick;

[0028] (4) Evenly spread a layer of laser powder on the upper layer of the epoxy resin varnish, sweep and press on the laser powder with a row sweeper, so that the laser powder is evenly attached to the glass brick, and stand until the epoxy resin varnish is dry;

[0029] (5) Spray the primer on the upper layer of the laser powder sheet, then bake at 150°C for 30 minutes, and cool;

[0030] (6) Use plastic printing to print the base screen paint on the base paint, and wait for it to dry or dry to obtain decorative tiles.

Embodiment 3

[0032] (1) Edge grinding, grinding, polishing, cleaning, and pressing of protective film on glass bricks;

[0033] (2) Use a plastic screen to print the pattern of the laser powder paste on the glass brick, bake at a temperature of 150°C for 30 minutes, and cool;

[0034] (3) Spray a layer of epoxy resin varnish evenly on one surface of the glass brick;

[0035] (4) Evenly spread a layer of laser powder on the upper layer of the epoxy resin varnish, sweep and press on the laser powder with a row sweeper, so that the laser powder is evenly attached to the glass brick, and stand until the epoxy resin varnish is dry;

[0036] (5) Spray the primer on the upper layer of the laser powder sheet, then bake at 150°C for 60 minutes, and cool;

[0037] (6) Use plastic printing to print the base screen paint on the base paint, and wait for it to dry or dry to obtain decorative tiles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The production process of a decoration board brick sprays a layer of epoxide resin varnish evenly on the surface, then a layer of laser powder fleck on the surface, sweeping and pressing the surface with the laser powder evenly attached on the glass brick, resting until drying of the varnish, spraying bottom paint on the laser powder fleck and baking in 150 degree for 30-60 minutes, cooling, net printing the bottom color paint with plastic rubber till its natural drying or baking it to dryness. It is cheap in cost, good in luster, straightness, transparency and intensity with strong cubic effect, free from erosion with long durability.

Description

technical field [0001] The invention relates to a process for producing decorative plate bricks, in particular to a process for producing decorative plate bricks made of glass. Background technique [0002] Today, with the development of science and technology and economy, the construction industry is also developing. In the construction industry, decoration is indispensable. Decoration materials are used for decoration, and decorative tiles are an important part of decoration materials. At present, the decorative tiles on the market mainly include polished tiles, antique tiles and glazed tiles. Polished tiles have the following disadvantages: the luminosity is unstable and uneven, and the color and luminosity of different batches of polished tiles are difficult to be the same; the anti-fouling ability is poor. Antique bricks have the following disadvantages: high water absorption, rough surface, and difficult to clean. The disadvantages of glazed tiles are: insufficient t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B11/06B28B11/00B44C1/00
Inventor 潘文建
Owner 潘文建
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com