Environment-friendly silver metal oxide rivet touch head producing method
An oxide, environmentally friendly technology, applied in the direction of nails, furnace types, mechanical equipment, etc., can solve the problem of cracks easily caused by rivets, and achieve the effect of overcoming low processing plasticity, reducing deformation, and simple process control
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0007] Example 1: The silver tin oxide wire with a diameter of φ2.38mm was put into a cold heading riveting machine, and an appropriate cold heading speed was adjusted to pre-head it into a φ3.9mm pre-heading ball. This pre-upset ball was annealed at 900°C for 1 hour. It was then cleaned and dried at 300°C for 1 hour. Put the cleaned and dried pre-upset balls into the vibration plate of the rotary rivet stamping machine, adjust the stamping speed to 50 grains / min, so that the pre-upset balls are stamped and formed at the stamping station of the rotary rivet stamping machine. φ5.0mm rivet contact, and then annealing the rivet at 900°C for 1 hour to obtain a soft, crack-free rivet product.
Example Embodiment
[0008] Example 2: The silver tin oxide wire with a diameter of φ2.38mm was put into a cold heading riveting machine, and an appropriate cold heading speed was adjusted to pre-head it into a pre-heading ball with a diameter of 3.9mm. This pre-upset ball was annealed at 150°C for 8 hours. It was then cleaned and dried at 110°C for 6 hours. Put the cleaned and dried pre-upset balls into the vibration plate of the rotary rivet stamping machine, adjust the stamping speed to 30 grains / min, so that the pre-upset balls are stamped and formed at the stamping station of the rotary rivet stamping machine. φ5.0mm rivet contact, and then anneal the rivet at 150°C for 8 hours to obtain a soft, crack-free rivet product.
Example Embodiment
[0009] Example 3: The silver tin oxide wire with a diameter of φ2.38mm was put into a cold heading riveting machine, and an appropriate cold heading speed was adjusted to pre-head it into a pre-heading ball with a diameter of 3.9mm. This pre-upset ball was annealed at 525°C for 4.5 hours. It was then cleaned and dried at 205°C for 3.5 hours. Put the cleaned and dried pre-upset balls into the vibration plate of the rotary rivet stamping forming machine, and adjust the stamping speed to 40 grains / min, so that the pre-upset balls are stamped and formed at the stamping station of the rotary rivet stamping and forming machine. φ5.0mm rivet contact, and then annealing the rivet at 525°C for 4.5 hours to obtain a soft, crack-free rivet product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap