Multifunctional aqueous adhesive and preparation method thereof

An adhesive and multi-purpose technology, applied in adhesives, natural rubber adhesives, monocarboxylate copolymer adhesives, etc., can solve the problems of water-based adhesives that cannot be popularized in large quantities, harmful solvents, flammable and explosive properties, etc. , to avoid the chance of poisoning and occupational diseases, the production process is simple, and the effect of wide application range

Active Publication Date: 2011-06-22
林润强
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a water-based adhesive to solve the above-mentioned deficiencies, which can solve the problems of insufficient adhesive force, harmfulness of solvents, and inflammable and explosive adhesives in solvent-based adhesives for bonding shoes, handbags, bags, and decoration materials. Sex, and avoid the high price of water-based polyurethane and water-based neoprene, which leads to the problem that water-based adhesives cannot be popularized in large quantities, and avoid the problem that hot-melt adhesives cannot be widely popularized due to equipment investment and unsuitability for manual operation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Put 10 parts of 120# solvent naphtha, 20 parts of toluene, and 3 isopropanol into the reaction kettle, add 10 parts of Yueyang Petrochemical SBS792 thermoplastic rubber, and add 30 parts of DA-103H emulsion. Stir and add 25 parts of rosin, 5 parts of Malayan rosin, 2 parts of K-12 additives, stir to dissolve, add 5 parts of deionized water to adjust the viscosity, cool, filter, and pack the material.

Embodiment 2

[0031] Add 25 parts of carboxylated styrene-butadiene modified emulsion, 2 parts of toluene, 0.5 parts of isopropanol, 35 parts of VAE705 emulsion, 60 parts of tackifying resin emulsion required by the present invention, 0.5 parts of DF-681 additive, and high-speed stirring. , Add 1 part of soft water to adjust the viscosity, cool and filter the package to discharge. The preparation method and process of the tackifying resin emulsion are as follows: put the rosin and the tackifying resin into the reactor, evacuate and fill with nitrogen, raise the temperature to be fully melted at a high temperature of 150°C, and adjust the stirring speed to slow during the process. Adjust to high-speed stirring, slowly add the pre-heated surfactant, then slowly drop the pre-heated water until the O / W (oil-in-water) phase inversion point, reduce the stirring speed to cool, filter and pack for later use .

[0032] Test items

[0033] Viscosity

[0034] It can be seen that both the above-men...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multipurpose aqueous adhesive, which comprises the following parts: 10-35% thermoplastic rubber or emulsion, 0. 5-35% solvent, 28-45% emulsion, 20-80% viscosifying resin or its emulsion, 0. 5-5% functional adjuvant and 1-20% water. The making method comprises the following steps: putting the solvent into autoclave; stirring at middle speed and adding thermoplastic rubberand its modifying product until dissolving completely; or putting into copolymerized rubber emulsion directly; stirring to add the viscosifying resin or the viscosifying resin in the invention; blending evenly; adding emulsion; fetching the sample to test the viscosity; adding fitful quantity of water and corresponding functional adjuvant according to the purpose and viscosity; dispersing at highspeed until even condition; cooling; filtering; packing; obtaining the product for shoe-making, hand pocket and decorative aspect with low cost.

Description

Technical field [0001] The invention relates to an adhesive, in particular to a water-based adhesive used for leather bonding, cloth bonding, furniture production, decorative material bonding and the like for shoemaking and handbag production. Background technique [0002] After years of accumulation and development, especially in the 1990s, my country's shoe and handbag industry has grown rapidly. China made 7 billion pairs of shoes last year, which is equivalent to making a pair of shoes for everyone in the world. China's shoe production accounts for 52% of global production and is the world's largest shoe manufacturer. The output and export volume of footwear products have steadily ranked first in the world. First of all, from the perspective of production capacity and production quantity, there are about 20,000 shoe-making enterprises in my country with more than 2 million employees. From the perspective of consumption quantity and market capacity, in recent years, nearly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J153/00C09J151/00C09J9/00C09J131/04C09J107/00C09J109/06C09J133/00
Inventor 林润强曾国良
Owner 林润强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products