Honeycomb ceramic material produced with alumina-chrome slag and its production process

A technology of honeycomb ceramics and production process, which is applied in the field of honeycomb ceramic raw materials and the production of honeycomb ceramics, which can solve the problems of poor anti-slag and anti-corrosion performance, sticking and blocking of iron oxide slag, short service life of honeycomb ceramics, etc. Achieve excellent anti-slag and anti-corrosion performance, good quality and performance, and sufficient source of raw materials

Inactive Publication Date: 2007-11-07
潘国明
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Honeycomb ceramics is an important key component in the field of environmental protection and energy saving. Various manufacturers have always used mullite, cordierite or corundum with good thermal shock resistance and high refractoriness as the best raw materials for making honeycomb ceramics. Because mullite The anti-slag and anti-corrosion properties of stone and cordierite raw materials are not very good, so that the service life of the current honeycomb ceramics is very short. The low-level production can only be used for 6-8 months, and the quality can only be used for 10-12 months. Especially Those whose furnace temperature is higher than 1300℃, or use dirty gas, SO 2 In the case of high corrosive substances such as CO, phosphate, etc., some honeycomb ceramics will be pulverized and collapsed after being put into use for about one month, or they will be completely stuck and blocked by iron oxide slag.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The aluminum chromium slag is put into a ball mill and pulverized into a fine powder of aluminum chromium slag, 8% binder and appropriate amount of water are added, kneaded, and then the mud is vacuum smelted, extruded, dried, and fired into honeycomb ceramics.

Embodiment 2

[0014] Take aluminum chromium slag and mullite with 80% of aluminum chromium slag and put it into a ball mill to crush into aluminum chromium slag fine powder, add 6% binder and appropriate amount of water, knead, and then carry out vacuum refining and extrusion Shaped, dried and fired into honeycomb ceramics.

Embodiment 3

[0016] Take aluminum chromium slag and cordierite with 15% aluminum chromium slag, put them into a ball mill and pulverize into fine powder, add 7% binder and appropriate amount of water, knead, then carry out vacuum refining, extrusion molding, drying, Fired into honeycomb ceramics.

[0017] Example 3

[0018] Take the aluminum-chromium slag and the sillimanite, andalusite and kyanite three-stone mixture with 55% of the aluminum-chromium slag and put it into a ball mill and pulverize it into a fine powder, add 9% of the binder and an appropriate amount of water, knead, and then carry out Vacuum smelting, extruding, drying, and firing into honeycomb ceramics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses one kind of honeycomb ceramic material produced with alumina-chrome slag added with 6-10 wt% binding agent. The production process is the following steps: compounding material, mixing and ball milling, adding binding agent and water and kneading, vacuum mixing, extruding to form, drying and sintering to produce honeycomb ceramic material. The present invention produces honeycomb ceramic material with alumina-chrome slag and has the advantages of rich material source, low cost, excellent anticorrosive performance and long service life.

Description

technical field [0001] The invention relates to a raw material of honeycomb ceramics and a production process for making honeycomb ceramics. Background technique [0002] Honeycomb ceramics is an important key component in the field of environmental protection and energy saving. Various manufacturers have always used mullite, cordierite or corundum with good thermal shock resistance and high refractoriness as the best raw materials for making honeycomb ceramics. Because mullite The anti-slag and anti-corrosion properties of stone and cordierite raw materials are not very good, so that the service life of the current honeycomb ceramics is very short. The low-level production can only be used for 6-8 months, and the quality can only be used for 10-12 months. Especially Those whose furnace temperature is higher than 1300℃, or use dirty gas, SO 2 In the case of high corrosive substances such as CO, phosphate, etc., some honeycomb ceramics will be pulverized and collapsed after ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B35/622
Inventor 潘国明
Owner 潘国明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com