Manufacture of ultra-fine material containing carbon and use thereof

A technology of ultra-fine materials and carbon materials, applied in the production of bulk chemicals, etc., can solve the problems of limiting the use range of ultra-fine carbon materials, and achieve the effect of expanding the application field and low price

Inactive Publication Date: 2008-01-23
张爱华
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] This limits the range of use of ultra-fine carbon materials to some extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The 10% polyacrylonitrile formamide solution is electrosprayed to obtain ultrafine polyacrylonitrile microspheres, and the ultrafine microspheres are carbonized to obtain ultrafine carbon microspheres.

Embodiment 2

[0021] The 30% polyacrylonitrile formamide solution is electrospun to obtain ultrafine polyacrylonitrile fibers, and the ultrafine fibers are carbonized to obtain ultrafine carbon fibers.

Embodiment 3

[0023] The 5% polystyrene ethyl acetate solution is sprayed into the water flow tube flowing in the same direction at a speed of 500,000 droplets / second through a 200-micron spray hole and collected in the collection pool. After drying, ultra-fine Polystyrene microspheres are obtained by carbonizing the ultrafine microspheres at high temperature to obtain ultrafine carbon microspheres.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses the preparation method and application of carbonic superfine materials, which is characterized in that the invention comprises the following steps: a. firstly disintermediate phase pitch materials capable of carbonizing are fluidized; b. secondly the fluidized materials capable of carbonizing are prepared into superfine materials; c. the carbonic superfine materials of the invention can be gained through carbonizing the superfine processed materials. The superfine carbonic materials prepared by the invention are used as functional materials. When using as the functional materials, the superfine carbonic materials has one or a plurality of following functions such as separating, transducing, catalyzing, storing, controlled release, structural support, absorbing and restoring. The invention is beneficial for improving the machining efficiency of the carbonic superfine materials and lowering the cost.

Description

Technical field: [0001] The present invention relates to the preparation and application of carbon-containing ultrafine materials, in particular to prepare non-mesophase pitch carbonizable materials into ultrafine fine material, and then carbonize the ultra-fine carbonizable material to obtain carbon-containing ultra-fine material. The ultrafine carbon material prepared by the invention is applied as a functional material. When this ultrafine carbon material is used as a functional material, it has one or more of the functions of separation, sensing, catalysis, storage, controlled release, structural support, adsorption, and repair. This technology can prepare carbon-containing ultrafine materials cheaply and on a large scale, so it is expected to help broaden and improve the application of carbon-containing ultrafine materials. Background technique [0002] Ultrafine carbon materials refer to materials including ultrafine carbon particles and ultrafine carbon fibers with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/02
CPCY02P20/54
Inventor 张爱华张继中
Owner 张爱华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products