Polypropylene plastics and manufacturing method thereof

A polypropylene plastic and polypropylene technology, applied in the field of polypropylene plastic and its production, can solve the problems of easy embrittlement and cracking, yellowing of polypropylene products, pollution, etc., and achieve the ability of not being easy to embrittle and crack, and low temperature Improvement, high efficiency, broad-spectrum effect

Inactive Publication Date: 2008-01-23
SHANGHAI PENGJING COMMODITIES
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it is dull, easy to be brittle and cracked at low temperature, and easily polluted by various harmful bacteria and molds like other plastics. Under suitable temperature and humidity conditions, it is easy to breed bacteria. Adding antibacte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 100 parts of polypropylene, 18 parts of barium sulfate, 0.15 parts of coupling agent, 0.1 part of antioxidant, 0.3 parts of dispersant, 0.2 parts of lubricant, 3.5 parts of silver-based antibacterial masterbatch, and 12 parts of elastomer.

[0030] Among them: the coupling agent is butyl titanate, the antioxidant is antioxidant 1010, the dispersant is sodium pyrophosphate, the lubricant is selected from stearic acid, and the silver-based antibacterial masterbatch is layered zirconium phosphate loaded with silver ions , a product of Shanghai Weilai New Material Technology Co., Ltd., wherein the weight of silver ions is 6%, and the elastomer is EPDM rubber.

[0031] The preparation method is as follows:

[0032] (1) After the high mixer is heated to 100°C, pour the barium sulfate filler into the high mixer, stir for 15 minutes to dry, add the coupling agent within 20 seconds, and mix for 7 minutes to obtain material A for later use ;

[0033] (2) Heat material A, antiox...

Embodiment 2

[0042] 100 parts of polypropylene, 20 parts of barium sulfate filler, 0.17 parts of coupling agent, 0.2 parts of antioxidant, 0.35 parts of dispersant, 0.3 parts of lubricant, 4.2 parts of silver antibacterial masterbatch, 13.5 parts of elastomer;

[0043] The coupling agent is propyl titanate, the antioxidant is antioxidant 168, and the dispersant is sodium polyphosphate.

[0044] The lubricant is selected from stearic acid; the silver-based antibacterial masterbatch is cubic zirconium phosphate loaded with silver ions, wherein the weight of silver ions is 2%, a product of Shanghai Weilai New Material Technology Co., Ltd.; the elastomer is poly Olefin elastomer, produced by DuPont Company of the United States;

[0045] Preparation method is with embodiment 1, wherein:

[0046] The extruder adopts three-stage sequential heating, the temperature is:

[0047] Level one: 175°C, level two 185°C, level three 215°C.

[0048] The silver-based antibacterial masterbatch is first dri...

Embodiment 3

[0051] 100 parts of polypropylene, 22 parts of barium sulfate filler, 0.2 part of coupling agent, 0.22 part of antioxidant, 0.4 part of dispersant, 0.35 part of lubricant, 5.2 parts of silver antibacterial masterbatch, 15 parts of polyolefin elastomer;

[0052] The coupling agent is butyl titanate; the antioxidant is antioxidant 1010, the dispersant is ammonium salt of phosphate, and the hydrophobic group is a hydrocarbon structure containing 10 carbon atoms; the lubricant is selected from stearic acid; silver The antibacterial masterbatch is glass powder loaded with silver ions, wherein the weight of silver ions is 4%, a product of Shanghai Weilai New Material Technology Co., Ltd.; the elastomer is selected from EPDM rubber.

[0053] Preparation method is with embodiment 1, wherein:

[0054] The extruder adopts three-stage sequential heating, the temperature is:

[0055] Level one: 155°C, level two 175°C, level three 195°C.

[0056] The detection method is the same as that ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glossaaaaaaaaaa
Antibacterial rateaaaaaaaaaa
Glossaaaaaaaaaa
Login to view more

Abstract

The invention provides a polypropylene plastic and the manufacture method. The components and the parts by weight are that: polypropylene 100, barium sulfate 14 to 26, coupling agent 0.1 to 0.3, antioxidant 0.1 to 0.3, dispersant 0.2 to 0.6, lubricant 0.2 to 0.6, silver antimicrobial mother material 2 to 7 and elastomer 7 to 16. The polypropylene plastic product produced by the antimicrobial polypropylene plastic with high luster and low-temperature resistance has better finish, is not easy to embrittle and break and has anti-bacterium effect. In addition, the polypropylene plastic product has surface finish not less than 70Cs (60 degree) and 24h antibacterial rate not less than 98 per cent, and has high efficiency and wide-adaptability and can keep good physical and chemical capability under the low temperature of minus 10 DEG C. to minus 20 DEG C..

Description

technical field [0001] The invention relates to a polypropylene plastic and a production method thereof, in particular to a high-gloss low-temperature resistant and antibacterial polypropylene plastic and a preparation method thereof. Background technique [0002] With the rapid development of society and the continuous improvement of people's living standards, plastic products occupy an indispensable position in people's daily life. Polypropylene is a non-toxic plastic with high heat resistance and good physical properties, which is widely used. But it is dull, easy to be brittle and cracked at low temperature, and easily polluted by various harmful bacteria and molds like other plastics. Under suitable temperature and humidity conditions, it is easy to breed bacteria. Adding antibacterial raw materials, this method is easy to make the color of polypropylene products turn yellow; at the same time, due to the uneven dispersion of the added antibacterial raw materials, the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08K9/02B29C47/92B29B9/12C08K5/10C08K5/521C08L23/16C08L23/00B29C48/92B29C48/95
CPCB29C48/92B29C2948/92704B29C2948/9259B29C2948/92885B29C2948/92895B29C48/95
Inventor 江凌戴喜平
Owner SHANGHAI PENGJING COMMODITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap