Boron-containing titanium-based amorphous solder for braze welding Si3N4 ceramic and preparation method thereof

A technology of ceramics and brazing filler metals, applied in the fields of Ti-Zr-Ni-Cu-B high-temperature active amorphous brazing filler metals and their preparation, brazing materials, boron-containing titanium-based amorphous brazing filler metals and their preparation fields, can solve the problem of Cu-Ti Solder can not be prepared and formed, poor high temperature performance, etc., to achieve the effects of good toughness, smooth sides, and smooth surface

Inactive Publication Date: 2008-04-09
JIANGSU UNIV OF SCI & TECH
View PDF0 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Technical problem: the purpose of the invention is to solve the current problem of brazing Si 3 N 4 The problem that ceramic Ag-Cu-Ti solder has poor high temperature performance and Cu-Ti solder cannot be prepared and shaped, provides a brazing Si 3 N 4 Ceramic boron-containing titanium-based amorphous solder and preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Component formula: the components and contents of the brazing filler metal are as follows: Zr: 20.0%; Ni: 20.0%; Cu: 20.0%; B: 0.2%; the rest is Ti.

[0028] Preparation:

[0029] (1) After pulverizing raw materials such as nickel plate (Ni), electrolytic copper block (Cu), sponge titanium (Ti), sponge zirconium (Zr) and copper-boron alloy, weigh the raw materials on an electronic balance according to the above formula, Cu, The purity of Ti and Ni is above 99.9%, the purity of Zr reaches 99.99%, and the mass fraction of B in the copper-boron alloy is 13.45%;

[0030] (2) Place the ingredients according to the above formula in the WS-2 type high vacuum Ar atmosphere protection non-consumable electric arc furnace. There are 5 copper crucibles in the electric arc furnace, and a piece of pure Ti sample is placed in one of the crucibles, and the remaining four The crucible can hold four ingredients of the same formula or different formulas at the same time;

[0031] (3) Befo...

Embodiment 2

[0043] Component formula: the components and contents of the brazing filler metal are as follows: Zr: 20.0%; Ni: 25.0%; Cu: 15.0%; B: 0.2%; the rest is Ti.

[0044] Preparation method: same as the preparation method of Example 1.

[0045] The melting temperature range of the brazing filler metal is 1207 ~ 1216K, using the amorphous brazing filler metal to vacuum braze Si 3 N 4 The high-temperature bending strength of ceramic joints is: 134MPa (673K); 116MPa (773K); 88MPa (873K).

Embodiment 3

[0047] Component formula: The components and contents of the brazing filler metal are as follows: Zr: 20.0%; Ni: 20.0%; Cu: 20.0%; B: 0.1%; the rest is Ti.

[0048] Preparation method: same as the preparation method of Example 1.

[0049] The melting temperature range of the brazing filler metal is 1192 ~ 1208K, using the amorphous brazing filler metal to vacuum braze Si 3 N 4 The high-temperature bending strength of ceramic joints is: 130MPa (673K); 101MPa (773K); 78MPa (873K).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting temperatureaaaaaaaaaa
Melting temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to braze welding Si3N4 ceramics containing the boron Ti-based amorphous solder and the preparation method thereof, and belongs to the brazing material in the field of amorphous state and metallurgy. The ingredients of the brazing material consist of the following according to the mass percent: Zr of 12.0-28.0 percent, Ni of 12.0-28.0 percent, Cu of 12.0-28.0 percent, and B of 0.05-0.5 percent, and the remains is Ti. The melting scope of the brazing material ranges 1,150K to 1,250K, and the brazing temperature is from 1,273K to 1,373K. The Ti-Zr-Ni-Cu-B amorphous braze vacuum braze welding Si3N4 ceramics, which is produced by the rapid solidification technology, has superior high-temperature performance to Ag-Cu-Ti solder and Ti-Zr-Ni-Cu solder. The tie-in high-temperature bend strength reaches 145MPa under 673K DEG,108MPa under 773K DEG, and still 93MPa under 873K DEG.

Description

Technical field: [0001] The invention relates to a brazing Si 3 N 4 The invention relates to boron-containing titanium-based amorphous solder for ceramics and a preparation method thereof, in particular to a Ti-Zr-Ni-Cu-B high-temperature active amorphous solder and a preparation method thereof, belonging to brazing materials in the fields of amorphous state and metallurgy. Background technique: [0002] Si 3 N 4 Ceramic is a kind of promising engineering structural ceramic material, its main application fields are heat engine, wear-resistant parts and heat exchanger, etc. It is an important material for manufacturing new ceramic engines. Its research and development has aroused people's high attention. Due to the shortcomings of ceramics such as poor processability, low ductility and impact toughness, low thermal shock resistance, and difficulty in manufacturing parts with large dimensions and complex shapes, it is usually necessary to form a composite structure with me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B37/00
Inventor 邹家生赵其章蒋志国赵宏权许志荣
Owner JIANGSU UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com