Cigarette tissue with variable permeating degree and method for producing the same
A technology of cigarette paper and air permeability, applied in separation methods, chemical instruments and methods, filter paper, etc., can solve the problems of slow particle thermal decomposition, poor actual effect, and paper inequality, achieve uniform pore distribution, and improve combustion conditions, the effect of increasing the pores
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] Zinc oxide powder additive was added to the foaming agent azodicarbonamide (thermal decomposition temperature 195°C), mixed evenly, and the thermal decomposition temperature was lowered to 160°C, which was used in the papermaking test. Use a cigarette paper air permeability tester to test the air permeability of the paper. The test process for the change of air permeability before and after heating the paper is as follows: mark the test position when testing the air permeability of the paper for the first time, and heat the paper at 170-230 ° C for 1-5 min. The quasi-mark again tests the air permeability of the position. Select more than 5 points to test the same sample, and the test results are shown in Table 1.
Example Embodiment
[0020] Example 2
[0021] According to the laboratory papermaking test, the change of air permeability of paper before and after heating, soaking and beating the weight of long fibers and short fibers in a ratio of 1:2, adding 30% calcium carbonate, guar gum and the content of the mass of the paper made 5% blowing agent azodicarbonamide, papermaking, drying. Use a cigarette paper air permeability tester to test the air permeability of the paper. The test method is the same as in Example 1, and the test results are shown in Table 1.
Example Embodiment
[0022] Example 3
[0023] The weight of long fibers and short fibers is 1:2, soaking, beating, guar gum and basic zinc carbonate accounting for 8% of the mass of the paper, making paper, and drying. Use a cigarette paper air permeability tester to test the air permeability of the paper. The test method is the same as in Example 1, and the test results are shown in Table 1.
[0024] Table 1 Comparison of changes in air permeability before and after heating of laboratory paper (1)
[0025] Air permeability change Δcu
[0026] It can be seen from Table 1 that after adding the foaming agent azodicarbonamide or basic zinc carbonate, the air permeability of the cigarette paper increases significantly after heating, reaching 9.37% and 14.63%, respectively.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thermal decomposition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap