Modifying reclaiming formulation for engineering plastic

A technology for engineering plastics and modification, applied in the field of plastic modification treatment, can solve problems such as uneconomical environment, pollution, corrosion of molding equipment and molds, and achieve good economic and social benefits.

Inactive Publication Date: 2008-07-02
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (1) Disposal by incineration or landfill, but this method is not only uneconomical but also causes environmental pollution, such as incineration will produce harmful gases such as sulfur dioxide, which is the main cause of acid rain
However, the landfill method of PC/ABS is not easy to degrade, which also causes great harm to the environment.
[0006] (2) Simple recovery and granulation of PC/ABS secondary materials without any modification, downgraded to ordinary plastics, although it is better than the f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0053] Example 1

[0054] First, take PC / ABS secondary materials, PC secondary materials, compatibilizers, toughening agents, brominated small molecule flame retardants, antimony flame retardants, antioxidants, ultraviolet absorbers and other ingredients, and press parts by weight The following composition formula blends all raw materials:

[0055] PC / ABS secondary material 81;

[0056] PC secondary material 5;

[0057] SMA 2;

[0058] MBS 5;

[0059] Decabromodiphenylethane 5;

[0060] Sb 2 O 3 2;

[0061] Antioxidant 0.3;

[0062]UV absorber 0.3.

[0063] Secondly, the above blended material is mixed and pelletized in an extruder;

[0064] Thirdly, the obtained mixing granulation can be made into finished products after modification of the secondary materials after injection molding.

[0065] The modified finished product was tested for performance and compared with the performance of the PC / ABS raw material alloy. The test results are shown in Table ...

Example Embodiment

[0069] Example 2

[0070] First, take PC / ABS secondary materials, PC secondary materials, compatibilizers, toughening agents, brominated small molecule flame retardants, antimony flame retardants, antioxidants, ultraviolet absorbers and other ingredients, and press parts by weight The following composition formula blends all raw materials:

[0071] PC / ABS secondary material 75;

[0072] PC secondary material 8;

[0073] SMA 2;

[0074] MBS 5;

[0075] Decabromodiphenylethane 7;

[0076] Sb 2 O 3 3;

[0077] Antioxidant 0.2;

[0078] UV absorber 0.2.

[0079] Secondly, the above blended material is mixed and pelletized in an extruder;

[0080] Thirdly, the obtained mixing granulation can be made into finished products after modification of the secondary materials after injection molding.

[0081] The modified finished product was tested for performance and compared with the performance of the PC / ABS raw material alloy. The test results are shown in Table...

Example Embodiment

[0084] Example 3

[0085] First, take PC / ABS secondary materials, PC secondary materials, compatibilizers, toughening agents, brominated small molecule flame retardants, antimony flame retardants, antioxidants, ultraviolet absorbers and other ingredients, and press parts by weight The following composition formula blends all raw materials:

[0086] PC / ABS secondary material 69;

[0087] PC secondary material 12;

[0088] SMA 4;

[0089] MBS 3;

[0090] Decabromodiphenylethane 9;

[0091] Sb 2 O 3 3;

[0092] Antioxidant 0.1;

[0093] UV absorber 0.1.

[0094] Secondly, the above blended material is mixed and pelletized in an extruder;

[0095] Thirdly, the obtained mixing granulation can be made into finished products after modification of the secondary materials after injection molding.

[0096] The modified finished product was tested for performance and compared with the performance of the PC / ABS raw material alloy. The test results are shown in Table ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a modified recovery formula of engineering plastic, which essentially comprises the following components calculated by weight proportion: 65-81 proportions of PC/ABS defective material, 5-12 proportions of PC defective material, 1-4 proportions of compatilizer, 4-8 proportions of flexibilizer, 5-10 proportions of brominated micromolecule flame retardant, 1-3 proportions of antimonic flame retardant, 0.1-0.3 proportions of antioxidant and 0.1-0.3 proportions of ultraviolet absorbent. The invention adopts the new toughener and flame retardant and is added with PC defective material to recycle PC/ABS defective material, thus leading the mechanical property and combustion performance of the PC/ABS defective material to meet the requirement of raw material while both the PC defective material and the PC/ABS defective material can be economically recycled. The invention has no additional burden on environment and better economic and social benefits.

Description

technical field [0001] The invention relates to the technical field of plastic modification treatment, in particular to a modified recycling formula for polycarbonate secondary materials and polycarbonate / acrylonitrile-butadiene-styrene copolymer (PC / ABS) secondary materials. Background technique [0002] PC / ABS alloy is a kind of engineering plastic with good comprehensive performance, which has the advantages of PC (Polycarbonate, polycarbonate) and ABS (Acrylonitrile-butadiene-styrene, acrylonitrile-butadiene-styrene copolymer). It has excellent mechanical and thermal properties, good formability and good stress cracking resistance, and is suitable for forming large and thin-walled parts. [0003] PC / ABS alloys are widely used in the automotive industry, household appliances, communication equipment such as mobile phones, office equipment such as calculators and printers, etc. The extensive use of PC / ABS alloys will inevitably produce a large number of inferior materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08K5/03C08L53/02C08L51/00C08L33/12C08K3/22C08K3/24
Inventor 岳瑟刘济林
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap