Material surface treatment composition, material and hydrophobic film prepared from the same

A technology of surface treatment and hydrophobic film, which is applied to the device for coating liquid on the surface, special surface, wax coating, etc., and can solve the problem that the fluidity of water droplets is not as good as expected

Active Publication Date: 2008-07-02
IND TECH RES INST
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Looking at the current commercially available car waxes from the perspective of the demand side, their performance still needs to be strengthened and improved. The function is that when coated on the surface of the car paint, it can fill up the unevenness on the paint to achieve the purpose of brightness and protection. Although some products use nanotechnology and cause a water drop effect with a contact angle of about 106 degrees, the water drop is fluid not as good as expected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material surface treatment composition, material and hydrophobic film prepared from the same
  • Material surface treatment composition, material and hydrophobic film prepared from the same
  • Material surface treatment composition, material and hydrophobic film prepared from the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Embodiment 1. the material surface treatment composition of the present embodiment

[0046] In order to further illustrate and verify the effect of the material surface treatment composition of the present invention, the composition of the present embodiment is prepared according to the following proportions: 100 parts by weight of wax; 20 parts by weight of silicone oil; 200 parts by weight of C6 to C30 carbon Hydrogen mixture oil; 10 parts by weight of micron titanium dioxide modified by polytetrafluoroethylene; 190 parts by weight of nano-titanium dioxide; and 5 parts by weight of resin, after mixing the components uniformly, the test of the subsequent embodiment can be carried out.

Embodiment 2

[0047] Embodiment 2. the detection of the material surface treatment composition of the present embodiment

[0048] The material surface treatment composition of the above-mentioned embodiment of the present invention is applied to the surface of the automobile steel plate with baking paint coating, and is detected with ASTM D3836-94 Standard Practice for Evaluation of Automotive Polish (Poland automobile evaluation and testing standard ASTM D3836-94) Its surface characteristic, obtained result is as follows table 1:

[0049] Table 1, ASTM D3836-94 test results

[0050] Test Item\Sample No.

[0051] It can be seen from the above table 1 that the hydrophobic film formed on the surface of the material by using the material surface treatment composition of the embodiment of the present invention does have the characteristics that meet the detection standards and meet the needs of car beauty.

Embodiment 3

[0052] Embodiment 3. Comparison of the water repellency of the material surface treatment composition of the embodiment of the present invention and commercially available goods

[0053] The following table 2 is a comparison of the water repellency of commercially available products and the material surface treatment composition of the embodiment of the present invention, and the product names are listed in Note 1 after Table 2:

[0054] Table 2, the performance comparison table of commercially available commodity and the embodiment of the present invention

[0055] Commercially available product A

Commercial goods B

Commercial goods C

Commercial goods D

This example

bead rolling

4

2

2

3

5

Water mark test

4

2

2

3

5

Contact angle

107

100

98

95

106

[0056] water damage test

none

many

many

many

many

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a composition used for material surface treatment, and a material with hydrophobic surface and a hydrophobic film which are prepared with the composition. The material surface treatment composition comprises wax, silicon oil, hydrocarbon mixture oil from C6 to C30, nano powder and resin; making use of the nano-powder of the composition, the modified material surface can be endowed with the property of low detention resistance against water caused by low surface energy and coarseness.

Description

technical field [0001] The invention provides a material surface treatment composition, and further, the invention also provides a material surface hydrophobic film containing the material surface treatment composition. Background technique [0002] Surface treatment science is an important subject in material science. Through surface treatment, the surface properties of materials can be changed, making it applicable to other fields. Surface treatment can be divided into permanent and temporary surface treatment. A representative example of permanent surface treatment is electroplating, which deposits a metal or alloy film on the surface of a material through an electrochemical method to produce a long-term property change on the surface of the material. However, this type of processing requires specific equipment to be carried out, and it is not easy for ordinary people to operate. [0003] Temporary surface treatment refers to the formation of a film on the surface of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D191/06B05D5/08B05D7/14B05D7/12C03C17/28C09D183/04C09D163/00C09D133/00
Inventor 郑鸿铰周文汉苏宗粲
Owner IND TECH RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap