A technology of heat exchanger and aluminum alloy foil, which is applied in the direction of metal rolling, metal rolling, metal processing equipment, etc., can solve problems such as complex production process, achieve process simplification, improve brazing performance, and save costs

Inactive Publication Date: 2008-07-16
河南顺源宇祥铝业科技有限公司
View PDF1 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method of milling, hot rolling, and then cold rolling is adopted during production, and the thickness is above...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1. Aluminum Alloy Foil Material and Production Method for Brazed Heat Exchanger

[0026] 1. Product ingredients:

[0027] Si

Fe

Cu

mn

Mg

Zn

Zr

Ti

Al

0.742

0.58

0.0552

1.34

＜0.05

1.82

0.143

0.0199

margin

[0028] 2. Production method:

[0029] (1) Melting

[0030] Add the qualified aluminum ingots and scraps into the flame reverberatory furnace, heat and melt them, stir them thoroughly, and analyze the components when the temperature reaches 730°C, and add Si, Fe, Cu, Mn, Mg, Zn, Zr, The composition of Ti is adjusted; after the composition is qualified, the temperature is adjusted, and the temperature of the molten aluminum alloy is 760°C.

[0031] (2) Static Furnace Refining

[0032] Transfer the aluminum alloy melt to the static furnace. During the transfer process and after filling the furnace, first use nitrogen and then carbon tetrachloride for r...

Embodiment 2

[0045] Embodiment 2, aluminum alloy foil material and production method for brazed heat exchanger

[0046] 1. Product ingredients

[0047] Si

Fe

Cu

mn

Mg

Zn

Zr

Ti

Al

0.888

0.428

0.0827

1.5

＜0.05

1.85

0.141

0.0241

margin

[0048] 2. Production method:

[0049] (1) Melting

[0050] Add the aluminum ingots and scraps that meet the requirements into the flame reverberatory furnace, heat and melt them, stir them fully, and analyze the components when the temperature reaches 740°C, and add Si, Fe, Cu, Mn, Mg, Zn, Zr, Ti according to the analysis results The composition is adjusted; the temperature is adjusted after the composition is qualified, and the temperature of the molten aluminum alloy is 765°C.

[0051] (2) Static Furnace Refining

[0052] Transfer the aluminum alloy melt to the static furnace. During the transfer process and after filling the furnace, first use nit...

Embodiment 3

[0064] Embodiment 3. Aluminum Alloy Foil Material and Production Method for Brazed Heat Exchanger

[0065] 1. Product ingredients:

[0066] Si

Fe

Cu

mn

Mg

Zn

Zr

Ti

Al

0.758

0.569

0.0592

1.28

＜0.05

1.82

0.165

0.0131

margin

[0067] 2. Production method:

[0068] (1) Melting

[0069] Add the aluminum ingots and scraps that meet the requirements into the flame reverberatory furnace, heat and melt them, stir them fully, and analyze the components when the temperature reaches 735°C, and add Si, Fe, Cu, Mn, Mg, Zn, Zr, Ti according to the analysis results Adjust the composition; adjust the temperature after the composition is qualified, and the temperature of the aluminum alloy melt is 755°C.

[0070] (2) Static Furnace Refining

[0071] Transfer the melt to the static furnace. During the transfer process and after filling the furnace, first use nitrogen and then carbon tet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an aluminum alloy foil material used in a brazing heat exchanger and a manufacturing method of the materials; wherein, indicated by weight percentage, the components of the material comprise0.50 to 1.00 of Si, less than or equal to 0.60 of Fe, 0.05 to 0.10 of Cu, 1.00 to 1.60 of Mn, less than or equal to 0.05 of Mg, 1.60 to 2.20 of Zn, 0.10 to 0.20 of Zr, 0.01 to 0.05 of Ti and unavoidable impurities and the allowance is Al; the materials are made through the manufacturing steps of melting, standing furnace refinement, grain refinement, online degassing, filtration, continuous cast rolling, cold rolling and finishing rolling. The aluminum alloy foil of the invention has the thinner thickness of 0.05mm; the tensile strength is more than 250N/mm<2>, which improves the brazing property; at the same time, the invention is simple in technique and saves the production cost by more than at least 50 percent compared with the method of hot rolling, and therefore, the aluminum alloy foil of the invention has better economic and social benefits.

Description

[0001] 1. Technical field: The present invention relates to an aluminum alloy foil material, in particular to an aluminum alloy foil material for a brazed heat exchanger and a production method thereof. 2. Background technology: [0002] At present, the aluminum alloy foils used in heat exchangers such as automotive air conditioners, intercoolers, heaters, and water tanks are mainly 3003 or 3A21 aluminum foils. The former is made of silicon, iron, copper and manganese, and the latter Made of raw materials such as silicon, iron, copper, manganese and titanium. Since these two aluminum foils have no anodic protection effect, the pitting corrosion of the aluminum foil will be increased during brazing; on the other hand, the manganese content in the 3003 and 3A21 aluminum foils is low, and the reduction of the manganese content causes the solidus temperature to decrease. Therefore, the solidus temperature of these two grades of aluminum foil is low, and deformation and collapse ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/10B23P15/00B21B1/46B21B37/16
Inventor 王镭张清莫振海朱应离
Owner 河南顺源宇祥铝业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap