Method for preparing amorphous alloy needle

An alloy needle and amorphous technology, which is applied in the field of preparation of alloy needles, achieves the effects of good biocompatibility, convenient operation, and excellent comprehensive performance

Inactive Publication Date: 2008-08-06
HARBIN INST OF TECH
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a method for preparing amorphous alloy needles in order to solve the problems that the current needle product preparation methods are prone to unsatisfactory physical and mechanical properties, microstructures, non-metallic inclusions, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing amorphous alloy needle
  • Method for preparing amorphous alloy needle

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0011] Specific Embodiment 1: In this embodiment, the preparation of amorphous alloy needles is carried out according to the following steps: the master alloy is placed in an inert atmosphere with a pressure of 0.02-0.07 MPa for arc melting, and then the master alloy melt is formed by copper mold suction casting. The amorphous alloy needle is obtained; the master alloy is Zr 51 Cu 24.22 Ni 14.06 Al 10.72 , Fe 36-45 co 2-5 Cr 15 Mo 14 C 15 B 6 Y 1-5 、Cu 44-54 Ti 30-38 Zr 6-12 Ni 6-9 、Ti 40 Zr 25 Ni 3 Cu 12 be 20 、Ti 40-45 Zr 2-5 f 4-6 Cu 37-43 Ni 7 Si 1 sn 0-9 or Ni 40-42 Ti 22-27 Zr 20-26 Al 7-9 Cu 5 Si 2-6 .

[0012] In conjunction with Fig. 1 and Fig. 2, the copper mold suction casting method of the present embodiment is illustrated: the master alloy melt is sucked in the metal copper mold cavity 2 of the amorphous alloy needle (the cavity 2 is composed of the left lobe mold 1 and the right lobe mold of the metal copper mold). The valve mold 3...

specific Embodiment approach 2

[0017] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the master alloy is arc-melted in an inert atmosphere with a pressure of 0.05 MPa. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0018] Embodiment 3: The difference between this embodiment and Embodiment 1 is that: vacuumize first and then fill with inert gas to form an inert atmosphere. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing amorphous alloy needles and relates to a method for preparing alloy needles. The invention solves the problem that an existing method for preparing needle products easily leads the products to appear that the mechanical property, the microstructure, non-metallic inclusions and the like are not accord with the requirements. The method of the invention for preparing the amorphous alloy needles comprises following steps: arranging master alloy into the inert atmosphere whose pressure is 0.02-0.07MPa to weld with electric arcs, then, adopting a water-cooled copper mold method by the master alloy to shape, and obtaining the amorphous alloy needles. The method of the invention for preparing the amorphous alloy needles is simple and the amorphous alloy needles which are prepared have excellent performance.

Description

technical field [0001] The invention relates to a method for preparing an alloy needle. Background technique [0002] Various types of needle products need to be widely used in fields such as textiles and medical treatment. Currently, the raw materials used are steels such as carbon tool steel, which contain harmful elements such as sulfur; and the preparation methods of existing needle products need to Raw materials are subjected to high-strength machining, which causes the current needle products to be prone to problems such as physical and mechanical properties, microstructure, and non-metallic inclusions that do not meet the requirements. In addition, the existing method for preparing needle products requires repeated machining and sharpening, which is inefficient and has large tolerances for products of the same type. Contents of the invention [0003] The present invention provides a method for preparing amorphous alloy needles in order to solve the problems that th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C45/10C22C45/00C22C1/03
Inventor 沈军孙亚娟魏先顺范洪波邢大伟
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap