Three-dimensional solid paint

A three-dimensional, three-dimensional coating technology, applied in coatings and other directions, can solve the problems of multi-color three-dimensional coatings such as toxicity, human health and environmental impact

Inactive Publication Date: 2008-08-27
SHANGHAI CHANGRUNFA PAINT
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the enrichment of home life, home decoration is becoming more and more diverse and complex. Many patterns drawn on drywall, wooden surfaces, and metal surfaces are inseparable from paints. Most of the colorful three-dimensional paints are poisonous. constitute an impact on human health and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A three-dimensional paint whose weight percentages are divided into: cellulose acetate 2wt%, vinyl acetate resin 1wt%, triethanolamine 0.6wt%, acrylic resin 22-33wt%, magnetic pigments 5-9wt%, diluent 69.5-48.5 wt%. The materials of the above formula are mixed at high speed to form a three-dimensional three-dimensional paint. With the cooperation of a special 3D mold, various three-dimensional patterns are formed by the magnetic field force between the resin and pigment molecules. It is widely used in plastic, wood, and metal materials. Surface decoration, simple process, easy construction, convenient operation, direct spraying, low cost on the product, good performance, green environmental protection, and meet ROHS and PAHS standards.

Embodiment 2

[0011] A three-dimensional paint whose weight percentages are divided into: cellulose acetate 3wt%, vinyl acetate resin 2wt%, triethanolamine 0.7wt%, acrylic resin 22~33wt%, magnetic pigment 5-9wt%, diluent 69.5-48.5 wt%. The materials of the above formula are mixed at a high speed to form a three-dimensional three-dimensional paint. With the cooperation of a special 3D mold, various three-dimensional patterns are formed by using the magnetic field force between the resin and pigment molecules. It is widely used in surface decoration of plastic, wood and metal materials. It has simple process, easy construction, convenient operation, direct spraying, low cost, good performance, green environmental protection, and meets ROHS and PAHS standards.

Embodiment 3

[0013] A three-dimensional paint whose weight percentages are divided into: cellulose acetate 4wt%, vinyl acetate resin 3wt%, triethanolamine 0.8wt%, acrylic resin 22~33wt%, magnetic pigment 5-9wt%, diluent 69.5~48.5 wt%. The materials of the above formula are mixed at a high speed to form a three-dimensional three-dimensional paint. With the cooperation of a special 3D mold, various three-dimensional patterns are formed by using the magnetic field force between the resin and pigment molecules. It is widely used in surface decoration of plastic, wood and metal materials. It has simple process, easy construction, convenient operation, direct spraying, low cost, good performance, green environmental protection, and meets ROHS and PAHS standards.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a three-dimensional stereoscopic coating, wherein the compositions of percentage by weight are that cellulose acetate butyrate 2-5wt%, vinyl chloride-acetate copolymer 1-3wt%, acrylic resin 22-33wt%, auxiliary agent 0.5-1.5wt%, magnetic pigment 5-9wt% and thinning agent 69.5-48.5wt%, the coating with the formula is widely used in plastic rubber, lumber and surface decoration of metal material, which has the advantages of simple technique, easy construction, convenient operation, low production cost, excellent performance and environmental protection, and the coating can be directly sprayed, which is accordance with POHS and PAHS standards.

Description

Technical field [0001] The invention relates to a field suitable for coating the surface of a substrate, in particular to a coating with a three-dimensional effect. Background technique [0002] As home life becomes more and more abundant, home decoration becomes more and more diversified and complicated. Many patterns depicted on dry walls, wood surfaces, and metal surfaces cannot be separated from paint. Most of the colorful three-dimensional paints are poisonous. Consists of the impact on human health and the environment. The Chinese patent CN1230578 provides a super strong three-dimensional three-dimensional coating, which is composed of cellulose, polyvinyl alcohol, white latex, titanium dioxide, talc, lithopone, glycerin, ethylene glycol, light calcium carbonate, and metaphosphate Calcium, color paste and water are mixed. When the invention is used, it can be directly sprayed on the wall to obtain patterns with different patterns. The invention has the advantages of unique ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02C09D7/12C09D131/04C09D101/12
Inventor 程强
Owner SHANGHAI CHANGRUNFA PAINT