Technique of preparing artificial stone

A preparation process and technology of artificial stone, applied in the direction of manufacturing tools, sustainable waste treatment, solid waste management, etc., can solve the problems of lack of wear resistance, pressure resistance, folding resistance, small effect of mesh cloth, safety accidents, etc. Achieve the effect of good seismic resistance, high surface and tensile strength, and increased seismic strength

Inactive Publication Date: 2009-02-04
青岛金炫建材有限公司
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, grid cloth (glass fiber mesh) is added to the interior of most inorganic composite artificial stones. The mesh cloth tightly bonds the various components of the artificial stone together, improving the tensile strength of the artificial stone, but for For larger artificial stone slabs and moulds, the role of the mesh cloth is very small, and it does not have strong wear resistance, pressure resistance, and folding resistance, and the shock resistance is also poor. For some demanding construction project, prone to safety accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0006] The specific embodiment one: the preparation method of the present invention according to the specific embodiment: (a) mold entry: according to weight percentage cement 20-25%, gypsum 5-10%, silica fume 10-15%, lithium carbonate 0.1-0.5%, 1-3% of special water-reducing agent, 1-2% of waterproofing agent, 5-10% of pigment, and 40-55% of sand are uniformly mixed and stirred, and then 15-20% of water is added and stirred again to obtain a mixture; (b) adding Wire mesh: Pour half of the mixture into the mold, put the wire mesh slightly smaller than the size of the mold, and press it tightly so that the wire mesh and the mixture stick together, pour the remaining half of the mixture into the mold, and vibrate , lead out the air bubbles to obtain a semi-finished product; (c) demoulding: place the semi-finished product for 1-2 hours to obtain a molded semi-finished product, and separate the molded semi-finished product from the mold; (d) curing: place the molded semi-finished p...

specific Embodiment approach 2

[0008] Embodiment 2: The difference from Embodiment 1 is that the added barbed wire is changed into steel bars, and other steps are the same as Embodiment 1.

[0009] In the present invention, harmless inorganic substances such as cement, gypsum, silica fume, industrial lithium carbonate, iron oxide pigment, special water reducing agent, built-in waterproofing agent, quartz sand, white sand, river sand and other colored sand, etc. Mixing, by adding barbed wire, the surface strength and tensile strength are increased, and the shock resistance is also increased, and the obtained product is odorless, non-toxic, non-radiation, fireproof, high surface and tensile strength, and good shock resistance.

[0010] Specific embodiments of the present invention: first weigh 700 grams of cement, 1.4 kilograms of sand, 140 grams of wollastonite powder, 3 grams of water reducing agent, 50 grams of waterproofing agent, 2 grams of pigment, and 1 gram of coagulant. Mix the above materials well, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation process of an artificial stone, relates to a decorative material of the artificial stone and belongs to the technical field of artificial stone material used in decoration. The invention more particularly relates to a preparation method of the artificial stone with high intensity. The product of the invention is prepared in a way that inorganic substances of cement, gypsum, siliceous dust, industrial lithium carbonate, ferric oxide pigment, a special water reducing agent, an inner-mixing waterproofing agent, quartz sand, white sand, river sand, other colored sand, and the like, which are harmless to human body are mixed and a wire gauze is added, thus improving the surface strength, tensile strength and earthquake resistant strength. The prepared product has the advantages of no smell, no toxicity, no radiation, fire protection, high surface strength, high tensile strength and good earthquake resistance.

Description

Technical field: [0001] The invention relates to an artificial stone decoration material, which belongs to the technical field of artificial stone for decoration, and in particular relates to a preparation method of high-strength artificial stone. Background technique: [0002] At present, grid cloth (glass fiber mesh) is added to the interior of most inorganic composite artificial stones. The mesh cloth tightly bonds the various components of the artificial stone together, improving the tensile strength of the artificial stone, but for For larger artificial stone slabs and moulds, the role of the mesh cloth is very small, and it does not have strong wear resistance, pressure resistance, and folding resistance, and the shock resistance is also poor. For some demanding construction Projects are prone to safety accidents. Invention content: [0003] The purpose of the present invention is to provide a preparation process of artificial stone, which can solve the existing pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B32/02B28B1/08B28B1/14C04B14/06C04B22/10
CPCC04B2111/54C04B2103/0008C04B28/14Y02W30/91C04B7/02C04B14/06C04B14/26C04B18/08C04B2103/302C04B2103/54C04B2103/65
Inventor 申东淳
Owner 青岛金炫建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com