A technology for infiltrating crystal waterproof and waterproof coatings, which is applied in the field of waterproof coating materials and inorganic powder infiltration crystal waterproof coatings, can solve problems such as inability to achieve waterproof effect, and achieve the effect of improving impermeability and strong penetration.
Inactive Publication Date: 2009-02-11
天津市耀新科技发展有限公司
View PDF0 Cites 42 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This kind of waterproof coating is made of Portland cement or ordinary Portland cement and refined quartz sand. After actual construction and application, it is found that this cement-based permeable crystalline waterproof coating is easy to stick to concrete because it is a rigid coating. However, after bonding, rigid cracks can still be produced, and the cracks become channels for water seepage and leakage, and cannot achieve waterproof effect
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
[0034] 20 parts of superfine quartz sand with a fineness of 70-100 mesh
[0035] Masterbatch 23 parts
[0036] High-efficiency retarding superplasticizer 3 parts
[0037] Polymer toughening agent (carboxymethyl cellulose) 1 part
[0038] Preparation process: screening→ingredients→feeding→mixing→inspection→packing and warehousing.
[0039] Screening: remove large particles of raw materials through a sieve; batching: batching according to the above formula; feeding: transport each raw material to the mixer; mixing: mix the raw materials evenly through the mixer; inspection: check the physical and chemical properties of the mixture; packaging Storage: Put the qualified inorganic powder infiltration crystalline waterproof material into bags or cans before storage.
[0040] The above formula is operated according to the preparation process of inorganic ...
[0060] The preparation process is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an inorganic powder infiltration crystalline water-proof material which consists of 45 to 55 portions of 600#silicate cement, 20 to 25 portions of ultra-thin quartz sands, 25 to 30 portions of master batches, 1 to 5 portions of effective retarding water reducers and 1 to 5 portions of macromolecular tougheners and is manufactured by feeding the materials into a stirrer to be uniformly stirred. The inorganic powder infiltration crystalline water-proof material is characterized by having the advantages of secondary anti-permeability capacity, durable water-proof performance, high sticking performance, acid resistance and alkali matter resistance; besides, the inorganic powder infiltration crystalline water-proof material have the capacity of growing an insoluble crystal in the pores and the micro cracks of a concrete substrate to plug the pores and the micro cracks, thereby improving the anti-permeability capacity of the concrete and achieving the goals of anti-permeability and anti-leakage. The inorganic powder infiltration crystalline water-proof material can be broadly applied to the water-proof projects of railways, roads, ports and docks, culverts, dams and pools as well as large underground projects.
Description
technical field [0001] The invention belongs to the technical field of building waterproof engineering, and relates to a waterproof coating material. Specifically, it is a waterproof and waterproof coating for flat and vertical surfaces of concrete structures such as highways, landfills, bridges, tunnels, and underground buildings. The leaking inorganic powder penetrates the crystalline waterproof coating. Background technique [0002] Concrete is a porous substance, and capillary pores and microcracks are the root causes of concrete leakage. Such as caused by deformation, including shrinkage, expansion, uneven subsidence, etc. caused by changes in temperature and humidity; caused by direct stress from external loads (dynamic and static loads). At present, most of the cement-based waterproof materials commonly used are surface-sealing waterproofing agents. The waterproof effect only acts on the surface and cannot automatically and deeply penetrate into the interior of the s...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more