Synthesis process of architectural waterproof material methyl sodium silicate

A technology for sodium methyl silicate and building waterproofing, applied in the direction of silicon organic compounds, etc., can solve problems such as increased cost, water resource pollution, social resource waste, etc., and achieve the effects of extending service life, protecting water resources, and preventing surface cracking

Inactive Publication Date: 2011-05-18
武汉春申高新技术有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the sodium hydroxide solution containing strong alkali will cause pollution of water resources
In order to meet the qualified water discharge standard, a large amount of basic chemical raw material acid can only be used to neutralize the waste liquid, which increases the cost of treating the waste liquid and causes a waste of social resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis process of architectural waterproof material methyl sodium silicate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] During implementation, the synthesis of organosilicon functional chemical material-sodium methyl silicate in the present invention is to mix cotton yarn bleaching waste liquid A and methyl silicate B in a weight ratio of A:B=4:1. The specific operation procedure is that after the cotton yarn bleaching waste liquid is settled in the sedimentation tank, it is poured into the reaction kettle according to the above formula as component A, and the methyl silicic acid of component B is added into the reaction kettle, stirred and mixed evenly, and heated to 90-95°C After 1-2h of heat preservation, precipitate and filter to obtain sodium methyl silicate.

[0011] Further introduce the implementation of the present invention below by embodiment:

[0012] 1. Take 800kg of cotton yarn bleaching waste liquid and put it into the reaction kettle, and gradually raise the temperature to 90°C.

[0013] 2. Take 200kg of methyl silicic acid and put it into the reaction kettle, stir evenl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a synthesis process of waterproof material methyl sodium silicate in construction industry. The synthesis process comprises the following steps: firstly, cotton bleaching efflue is infiltrated into a reaction vessel; then methyl- silicic acid is added for forming mixture; the mixture is greatly stirred and heated until the temperature reaches 90 to 95 DEG C; the temperature is kept for 2hs, and the methyl sodium silicate solution is obtained after the processes of sedimentation and filtration. The waterproof material methyl sodium silicate has a simple process and low manufacturing cost, particularly the waste cotton bleaching liquor is selected and used as main raw materials, not only the waste is converted to useful materials and a great deal of water resource issaved, but also the general goal of saving resources, protecting the environment and pursuing economic efficiency in human production is realized.

Description

technical field [0001] The invention relates to the manufacture of building waterproof materials, in particular to a synthesis process of sodium methyl silicate, a waterproof material used in the building industry. Background technique [0002] The sustainable development of human beings requires human beings to start from resource conservation, environmental protection and economic benefits. At present, the production of organosilicon-sodium methyl silicate, a functional chemical building material, is mainly made by mixing methyl silicic acid and sodium hydroxide aqueous solution, heating the mixture at 90-95°C for 2 hours, adding water, and filtering to obtain methyl silicon Sodium acid solution. This method will consume a large amount of basic chemical raw material sodium hydroxide, and the production cost is relatively high. In addition, the current cotton yarn bleaching process in the textile industry is to mix water, sodium hydroxide, hydrogen peroxide, etc. into a h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07F7/04
Inventor 黄菁华
Owner 武汉春申高新技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com