Laminated wood cabinet-work high-intensity decoration sheet material and preparation method thereof

A decorative board and joinery technology, applied in the direction of wood layered products, wood processing equipment, wooden veneer joints, etc., can solve the problem of weak joints of wood boards, poor strength and stain resistance of decorative boards, and easy deformation of base boards Or expansion and other problems, to achieve the effect of reducing environmental pollution, prolonging the construction period, increasing costs, beautiful decoration and high overall strength

Inactive Publication Date: 2009-07-15
秦拥均
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the surface of ordinary joinery decorative boards is laminated with resin-impregnated paper and small wood boards as the base layer. This kind of decorative boards has poor strength and stain resistance, and the board surface is easy to warp and burst when exposed to water and moisture. , the interface of ordinary small wood boards is not firm, the base board is easy to deform or expand, the glue strength and aging resistance are low, it is used for building decoration, the furniture is not strong enough, and the quality cannot be guaranteed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1. The preparation of the substrate board:

[0026] Cut softwood pine or poplar into standard equal-size materials with a length of 40-250 cm, a width of 2-10 cm, and a thickness of 0.8-3 cm according to the shape of the wood itself, planed and set aside;

[0027] 2. Drying: dry the spare standard isometric finished material in step 1, and set aside;

[0028] 3. Finger-joining: Mill the spare standard equal-size material after drying in step 2 into a zigzag shape, apply glue, press and join to form a profile with a length of 240-250 cm, equal width, and equal thickness, and set aside;

[0029] 4. Glue application: Apply glue to the surface of the spare profile in step 3 on the glue spreader, the glue amount is 250 g / m2, and age for 15 minutes after glue coating, then set aside;

[0030] 5. Jigsaw board: Put the spare profiles coated and aged in step 4 on the jigsaw machine. The frame length of the jigsaw machine workbench is 240-245 cm, and the width is 120-125 cm. Sl...

Embodiment 2

[0039] 1. The preparation of the substrate board:

[0040] Cut softwood pine or poplar into standard equal-size materials with a length of 40-250 cm, a width of 2-10 cm, and a thickness of 0.8-3 cm according to the shape of the wood itself, planed and set aside;

[0041] 2. Drying: dry the spare standard isometric finished material in step 1, and set aside;

[0042] 3. Finger-joining: Mill the spare standard equal-size material after drying in step 2 into a zigzag shape, apply glue, press and join to form a profile with a length of 240-250 cm, equal width and equal thickness, and set aside;

[0043] 4. Glue application: Apply glue to the surface of the spare profile in step 3 on the glue spreader, the glue amount is 300 g / m2, and age for 30 minutes after glue coating, and set aside;

[0044] 5. Jigsaw board: Put the spare profiles coated and aged in step 4 on the jigsaw machine. The frame length of the jigsaw machine workbench is 240-245 cm and the width is 120-125 cm. Slabs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a glulam joinery high-strength decorative plate and a preparation method thereof. The decorative plate comprises a basal plate and decorative veneers at two sides of the basal plate; the upper surface and the lower surface of the basal plate are combined with reinforcing laminates; and the outer surfaces of the reinforcing laminates are combined with decorative veneers. The preparation method for the plate comprises the technological steps of preparation of basal plate materials, drying, finger joint, glue spreading, plate splicing, hot pressing, polishing, combination of reinforcing plates, second polishing, combination of decorative veneer, cutting, edging and packing. The decorative plate has good integrity, high strength, age resistance, high selectivity of veneer patterns, novel style, rich variety, attractive color and smooth texture, and can be widely used in manufacturing industry of veneers such as furniture, closets, architectural upholstering and decoration and the like.

Description

technical field [0001] The invention relates to a decorative board, in particular to a laminated joinery high-strength decorative board suitable for decorative surfaces of furniture, cupboards, and home decoration, and a preparation method thereof. technical background [0002] In the prior art, the surface of ordinary joinery decorative boards is laminated with resin-impregnated paper and small wood boards as the base layer. This kind of decorative boards has poor strength and stain resistance, and the board surface is easy to warp and burst when exposed to water and moisture. , The interface of ordinary small wood boards is not firm, the base board is easy to deform or expand, the glue strength and aging resistance are low, it is used for building decoration, the furniture is not strong enough, and the quality cannot be guaranteed. Contents of the invention [0003] One of the objectives of the present invention is to provide a high-strength decorative board for glulam j...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B27D1/10B32B21/13B32B5/00
Inventor 秦拥均
Owner 秦拥均
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap