Technical method for producing heat-resisting alloy steel casting below 1100 DEG C

A process method and technology of heat-resistant alloys are applied in the field of heat-resistant alloy steel castings to achieve the effects of good casting performance and machinability, reducing production costs and being widely used.

Active Publication Date: 2009-10-21
WUXI YELONG PRECISION MACHINERY
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above defects, the purpose of the present invention is to provide a process method for heat-resistant alloy steel castings below 1100 °C with good casting performance and machinability and low production cost, so as to solve the problems of the existing process methods. insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] According to the process method for heat-resistant alloy steel castings below 1100°C described in the embodiments of the present invention, the chemical composition of the alloy steel casting raw materials is: C=0.42%, Cr=25%, Ni=18%, Si =1.2%, Mn=0.6%, P=0.03%, S=0.12%; the microstructure of the material used is composed of austenite and interdendritic chromium carbide, and the process method adopted includes the following steps:

[0009] (1) Put the above raw materials into the bottom of the vacuum furnace in order, put other elemental materials in the material distribution box for use, put the casting mold in a medium temperature furnace at 900°C-950°C for 1-1.5 hours, and take it out quickly Then put it on the iron plate of the vacuum melting furnace;

[0010] (2) Preheat the stainless steel raw material to 200°C-300°C and put it into the induction furnace. After all the furnace materials are melted, add appropriate additive elements for refining. When the temperatu...

Embodiment 2

[0014] According to the process method for heat-resistant alloy steel castings below 1100°C described in the embodiments of the present invention, the chemical composition of the alloy steel casting raw materials is: C=0.48%, Cr=27%, Ni=22%, Si =1.2%, Mn=3.0%, P=0.14%, S=0.12%; the microstructure of the material used is composed of austenite and interdendritic chromium carbide, and the process method adopted includes the following steps:

[0015] (1) Put the above raw materials into the bottom of the vacuum furnace in order, put other elemental materials in the material distribution box for use, put the mold in a medium temperature furnace at 850°C-950°C for 1-1.5 hours, and quickly take it out Then put it on the iron plate of the vacuum melting furnace;

[0016] (2) Preheat the stainless steel raw material to 100°C-300°C and put it into the induction furnace. After all the furnace materials are melted, add appropriate additive elements for refining. When the temperature reach...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a technical method for producing a heat-resisting alloy steel casting below 1100 DEG C. The chemical components of the materials of the alloy steel casting are as follows: not less than 0.42 percent and not more than 0.48 percent of C, not less than 25 percent and not more than 27 percent of Cr, not less than 18 percent and not more than 22 percent of Ni, 1.2 percent of Si, not less than 0.6 percent and not more than 3.0 percent of Mn, not less than 0.03 percent and not more than 0.14 percent of P, and 0.12 percent of S; the microstructure of the adopted materials comprises austenitic and interdendritic chromium carbide.. The invention has the advantages of good casting performance and machining performance, significant reduction of production cost and being widely applied to the production of vehicle turbine shells.

Description

technical field [0001] The invention relates to the technical field of preparation of heat-resistant steel castings, in particular to a process method for heat-resistant alloy steel castings below 1100°C. Background technique [0002] Facing the implementation of Euro V emission standards in the automobile industry, the efficiency of automobile engines will be greatly improved, and the exhaust gas temperature of the engine can reach 900°C-1150°C; currently there are heat-resistant alloy stainless steel materials specified in European standards, ASTM standards and ISO standards. Poor casting performance, poor machining and cutting performance, etc., such as automotive engine exhaust system components, are suitable for heat-resistant steel castings at specific temperatures. The existing ferritic stainless steel refers to stainless steel with a chromium content of 11%-30%, a body-centered cubic crystal structure, and a ferritic structure in use; ferritic stainless steel plates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/60C22C30/04C21C7/076C21C7/072C21D1/26
CPCY02P10/20
Inventor 罗琪朱瑞卿张良楠
Owner WUXI YELONG PRECISION MACHINERY
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com