Method for preparing isosorbide modified polyester

A technology of isosorbide and modified polyester, which is applied in the field of polyester preparation, can solve the problems of increased probability of molecule ring formation, decrease of molecular weight, and increase of dispersion, so as to reduce the probability of product molecule ring formation and reduce raw materials loss, molecular weight reduction effect

Active Publication Date: 2009-12-02
NANJING UNIV OF TECH
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First of all, at this temperature, the monomer will be distilled out together with the by-products, resulting in serious waste of raw materials
Secondly, ether bonds are easier to form at this tempera

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] DMT (194g), ethylene glycol (68g), isosorbide (10g), bismuth trifluoromethanesulfonate (0.67g) and 1010 antioxidant (0.1g) were added to the polymerization reactor equipped with rectification tower , heat and stir it. When the temperature reached 160°C, it was evacuated to remove by-products, and the temperature was raised to 200°C within 15 minutes, and the heating time was 60 minutes. Then the temperature was raised to 230°C, the pressure was around 2mmHg, and the heating time was 90min.

Embodiment 2

[0024] DMT (194g), ethylene glycol (93g), isosorbide (10g), bismuth trifluoromethanesulfonate (1.69g) and 1010 antioxidant (0.1g) were added to the polymerization reactor equipped with rectification tower , heat and stir it. When the temperature reached 160°C, it was evacuated to remove by-products, and the temperature was raised to 200°C within 15 minutes, and the heating time was 60 minutes. Then the temperature was raised to 240°C, the pressure was around 2mmHg, and the heating time was 90min.

Embodiment 3

[0026] DMT (194g), ethylene glycol (93g), isosorbide (20g), bismuth trifluoromethanesulfonate (3.37g) and 1010 antioxidant (0.1g) were added to the polymerization reactor equipped with rectification tower , heat and stir it. When the temperature reached 160°C, it was evacuated to remove by-products, and the temperature was raised to 190°C within 15 minutes, and the heating time was 45 minutes. Then the temperature was raised to 230°C, the pressure was around 2mmHg, and the heating time was 90min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing isosorbide modified polyester. The method takes dimethyl terephthalate (DMT) or pure terephthalic acid (PTA), glycol and isosorbide as monomers and trivalent bismuth metal as a catalyst to prepare the polyester at enough temperature and pressure through the prior polymerization equipment. Bi (III) is a heavy metal ion with the lowest toxicity, and the nature is very important when polymer is applied to medicaments, human bodies, agriculture and the like. The method uses the trivalent bismuth metal such as trifluoromethanesulfonate as the catalyst, can reduce temperature required by reaction, decrease the loss of raw materials in a system and simultaneously reduce occurrence probability of side reaction, and does not reduce the molecular weight therewith.

Description

technical field [0001] The invention relates to a preparation method of polyester, in particular to a preparation method of isosorbide-modified polyester. Background technique [0002] Polyester (PET) is a polymer compound, which is produced by polycondensation of terephthalic acid and ethylene glycol to produce polyethylene terephthalate. PET has good fiber-forming properties, mechanical properties, wear resistance, creep resistance, low water absorption and electrical insulation properties. Polyester is mainly used to produce polyester fiber (polyester), and is widely used in light industry, machinery, electronics, food packaging and other industrial fields as non-fiber films, plastics, packaging containers, adhesives, and coating products. However, with the development of society, ordinary polyester can no longer meet the growing needs of people's lives and industrial fields. [0003] The scientific name of isosorbide is 1,4:3,6-dianhydro-D-sorbitol, which can be prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/66C08G63/672C08G63/85
Inventor 李振江张昊夏海东张钰铖孙晓日赵红婷韦萍欧阳平凯
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap