Hydraulic PU crazy horse resin for synthetic leather

A technology of crazy horse resin and synthetic leather, which is applied in the field of water-based PU crazy horse resin for synthetic leather. Hand feeling is not good and other problems, to achieve the effect of excellent comprehensive effect, coating solvent resistance, good crazy horse discoloration effect

Inactive Publication Date: 2009-12-16
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in solvent-based Crazy Horse resin will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good;
[0005] 2. The organic solvent contained in the solvent-based Crazy Horse resin is not only expensive, smelly, easy to pollute the environment, but also has safety hazards such as flammability and explosion;
[0006] 3. Synthetic leather products prepared by solvent-based Crazy Horse resin have poor visual effects, viscosity, stability, hand touch and other comprehensive effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1. Water-based PU Crazy Horse resin for synthetic leather is composed of the following raw materials: 100 kg of aliphatic polyurethane emulsion (30% solid content), 90 kg of ordinary tap water, 13 kg of silica discoloration powder, 8 kg of matting powder, and smooth silicone oil 3 kg of water-based polyurethane thickener, 5 kg of silicone defoamer, 3 kg of silicone leveling agent, and 6 kg of 0.2 longan yellow fluff.

[0029] 2, the preparation method of water-based PU Crazy Horse resin for synthetic leather of the present invention is as follows:

[0030] ①Select 100 kg of aliphatic polyurethane emulsion (30% solid content), 13 kg of silica discoloration powder, 8 kg of matting powder, 3 kg of silicone oil slip agent, 5 kg of silicone defoamer, 5 kg of silicone fluid 3 kg of leveling agent, 90 kg of tap water, stirred for 2 hours, fully mixed and set aside;

[0031] 2. Grinding and filtering the mixture obtained in step 1. reaction;

[0032] ③ Take the mixture obtain...

Embodiment 2

[0038] 1. Water-based PU Crazy Horse resin for synthetic leather is composed of the following raw materials: 90 kg of aromatic polyurethane emulsion (30% solid content), 80 kg of ordinary tap water, 16 kg of silica discoloration powder, 8 kg of matting powder, and smooth silicone oil 6 kg of agent, 4 kg of non-ionic polyurethane polymer thickener, 8 kg of silicone defoamer, 2 kg of silicone leveling agent, and 10 kg of 0.2 longan yellow fluff.

[0039] 2, the preparation method of water-based PU Crazy Horse resin for synthetic leather of the present invention is as follows:

[0040] ①Select 90 kg of aromatic polyurethane emulsion (30% solid content), 16 kg of silica color changing powder, 8 kg of matting powder, 6 kg of silicone oil slip agent, 8 kg of silicone defoamer, and 8 kg of silicone fluid according to the above proportions 2 kg of leveling agent and 80 kg of tap water, stirred for 3 hours, fully mixed and set aside;

[0041] 2. Grinding and filtering the mixture obta...

Embodiment 3

[0049] 1. Water-based PU Crazy Horse resin for synthetic leather is composed of the following raw materials: 70 kg of aliphatic polyurethane dispersion (30% solid content), 60 kg of ordinary tap water, 10 kg of silica discoloration powder, 2 kg of matting powder, silicone oil 2 kg of refreshing agent, 1 kg of non-ionic polyurethane polymer thickener, 4 kg of silicone defoamer, 1 kg of silicone leveling agent, and 4 kg of 0.2 longan yellow fluff.

[0050] 2, the preparation method of water-based PU Crazy Horse resin for synthetic leather of the present invention is as follows:

[0051] ①Select 70 kg of aliphatic polyurethane dispersion (30% solid content), 10 kg of silica discoloration powder, 4 kg of matting powder, 4 kg of silicone oil slip agent, 4 kg of silicone defoamer, 4 kg of silicone 1 kg of leveling agent, 60 kg of tap water, stir for 3 hours, fully mix and set aside;

[0052] 2. Grinding and filtering the mixture obtained in step 1. reaction;

[0053] ③ Take the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydraulic PU crazy horse resin for synthetic leather; the hydraulic PU crazy horse resin is constituted by the following raw materials by weight percentage: 35-45 percent of waterborne polyurethane, 30-40 percent of water, 5-8 percent of silicon dioxide color changing powder, 1-3 percent of silicone oil slip agents, 1-4 percent of extinction powder, 0.5-1 percent of organic silicon flatting agent, 2-5 percent of silicone defoaming agents, 0.5-2 percent of waterborne polyurethane thickeners and 2-5 percent of villus. The hydraulic PU crazy horse resin for synthetic leather takes water as solvent, toxic solvents such as dimethyl fomamide and butanone are replaced, therefore, the hydraulic PU crazy horse resin has non-inflammable, safe, environmental-protection, cost-saving performances, and the crazy horse resin has the advantages of good film forming property, firm adhesion, solvent-proof, cold-resistance, hydrolyzation-resistance and heat-proof ageing coating. The finished products manufactured by the crazy horse resin has the advantages of full handle, good crazy horse color-changing effect, fine and smooth texture, good air permeability and the like.

Description

technical field [0001] The invention relates to a resin for synthetic leather, in particular to a water-based PU Crazy Horse resin for synthetic leather. Background technique [0002] At present, synthetic leather products have gradually become a popular trend in the future, and synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is a canvas PU material with good tensile strength. In addition to being coated on the top of the base fabric, the base fabric can also be included in the middle, so that the existence of the base fabric cannot be seen from the outside. PU leather has physical properties. Good, tortuous resistance, good softness, high tensile strength, and breathability, so PU leather is widely used in footwear fabrics or weight-bearing parts of luggage. [0003] At present, the Crazy Horse resin for synthetic leather sold on the market is usually solvent-based Crazy Horse resin, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M13/50
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com