Method for preparing piezoelectric polymer functional film with ordered micro-cellular structure by using template

A technology of piezoelectric polymer and microporous structure, which is applied in the direction of microstructure technology, microstructure device, and processing microstructure device, etc., which can solve the problem that the mechanical properties and charge storage capacity of porous membranes cannot be effectively controlled or precisely controlled Porous membrane microstructure parameters and other issues, to achieve the effect of simple preparation process

Inactive Publication Date: 2010-01-13
TONGJI UNIV
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current preparation technology cannot precisely control the microstructure parameters of the porous membrane, an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing piezoelectric polymer functional film with ordered micro-cellular structure by using template
  • Method for preparing piezoelectric polymer functional film with ordered micro-cellular structure by using template
  • Method for preparing piezoelectric polymer functional film with ordered micro-cellular structure by using template

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] please see figure 1 , 3 , 4, 5, 6, 7, 9 and 10. First engrave the cells on the commercially available composite copper plate to make template 4, the cells are square, and the square area is 1mm 2, the spacing between the squares is d=0.5mm, and the concave dimension of the spacing is h=0.5mm. A template 4 with a concave-convex ordered pattern was obtained. Select the PTFE with a porosity of 90% produced by DuPont as the organic polymer film 2-1, get an iron plate (steel plate) as the base plate 6, place the template 4 on the base plate 6, the pattern of the template 4 is upward, and the template 4 The organic polymer film 2-1 is placed on the pattern of the organic polymer film 2-1, and the hard 0.2mm PTFE gasket 5 and the bottom plate 6 are stacked in turn on the organic polymer film 2-1. Then, the pressure is applied under the pressure of 3Mpa for 5s, and then the bottom plate 6 and the bottom plate are removed. Gasket 5, removes organic polymer film 2-1 from temp...

Embodiment 2

[0038] please see figure 2 , 3 , 4, 5, 6, 8, 9 and 11. Composite copper plate template is used, the cells are square, and the square area is 1mm 2 , the spacing between the squares is d=0.5mm, and the concave dimension of the spacing is h=0.5mm. The film 2-1 is made of 25 μm dense PTFE produced by DuPont Company, the gasket 5 is made of rubber, and the pressure is applied under a pressure of 6 MPa for 2 minutes to prepare a double-sided concave-convex pattern ordered porous polymer single-layer film 2-3, followed by hot pressing Process: Place the double-sided concave-convex pattern ordered porous polymer single-layer film 2-3 in the middle of the two dense films, place the protective plate 7 and the hard plate 8 on the upper and lower sides of the two dense films, and the two dense films are high melting point films 1 And low-melting point film 3, high-melting point film 1 and low-melting point film 3 all adopt the dense FEP of 12.5 μm produced by DuPont Company, the pres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a piezoelectric polymer functional film with an ordered micro-cellular structure by using a template, and relates to a preparation technique of the piezoelectric polymer functional film with the ordered micro-cellular structure. The method firstly prepares a template (4) with a concave-convex ordered pattern, then prepares an ordered porous polymer single-layer thin film (2) which shows a pattern corresponding to the concave-convex ordered pattern of the template (4), then clamps the ordered porous polymer single-layer thin film (2) between two dense films, and carries out hot-pressing to form the piezoelectric polymer functional film with the ordered micropore structure. The method has simple technique, not only can obtain an electromechanical functional film with high thermostability and high pressure flexibility, and has more outstanding advantages of the capability of precisely controlling the microstructure of the film and electric charge of the storing space. The obtained functional film can be used for manufacturing electroacoustic sensors, acoustoelectric sensors, infrasonic wave sensors, ultrasonic sensors, plate loudspeakers, actuators and robot skin and the like, and has wide application prospect in the fields of communication, public security, control, medical treatment, robots, military and the like.

Description

technical field [0001] The invention discloses a method for preparing a piezoelectric polymer functional film with an ordered microporous structure by using a template, and relates to a preparation process for a piezoelectric polymer functional film with an ordered microporous structure. It belongs to the technical field of functional materials. Background technique [0002] Some non-polar microporous polymer films have both piezoelectric and electret properties after proper electric polarization treatment, and are named piezoelectric electret (piezoelectret) or ferroelectret (ferroelectret) , is a new member of the family of electromechanical sensor materials. Piezoelectric electrets are different from traditional piezoelectrics and ferroelectrics in that the material itself is a non-polar material, and its piezoelectric effect is derived from the air gap ionization captured by the two solid medium walls of the hole during the electric polarization process. The charges of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B81C5/00B81C3/00H01L41/22H01L41/45
Inventor 张晓青曹功勋潘道胜王学文孙转兰夏钟福
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap