Single-wall heat-shrinkable tube and preparation method thereof

A heat-shrinkable tube, heat-shrinkable tube technology, applied in the direction of cable joints, etc., to achieve the effect of low longitudinal shrinkage

Inactive Publication Date: 2011-08-31
江苏达胜热缩防护用品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ordinary heat shrinkable tubes can no longer meet these requirements at the same time, which brings us a new topic, that is, it is necessary to develop a heat shrinkable tube that can not only be waterproof and sealed, but also have certain mechanical strength, good electrical properties and chemical properties. A new type of heat shrinkable product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A single-wall heat-shrinkable tube is composed of wall material, wherein the wall material is composed of 80 parts of polyolefin mixed resin and 20 parts of auxiliary agent according to the parts by mass;

[0027] By mass percentage: the polyolefin mixed resin is a polyolefin mixed resin prepared by melt blending four kinds of polyolefin materials: 1-30% EVA630, 1-20% EVA421, 20-50% EVA283 and 10-30% EVA220 ;

[0028] The auxiliary agent is composed of paraffin, antioxidant, anti-copper agent, processing stabilizer and sensitizing cross-linking auxiliary agent; wherein the antioxidant tetrakis (β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid) 1-3 parts of pentaerythritol; anti-copper agent MDA-1024 (hydroxyl-terminated polybutadiene acrylonitrile liquid rubber) 0.5-1 part; processing stabilizer rare earth composite stabilizer (REC-LS-D or REC-LS- F) 0.02-2 parts; 2-4 parts of smoke suppressant zinc borate; 1-2 parts of chemical crosslinking aid TMP (trimethylolpro...

Embodiment 2

[0040] A single-wall heat-shrinkable tube is composed of a wall material. According to the mass parts, the wall material is composed of 80 parts of polyolefin mixed resin and 20 parts of auxiliary agent;

[0041] The polyolefin mixed resin is a polyolefin mixed resin prepared by melt blending four kinds of polyolefin materials of 15% EVA630, 20% EVA421, 45% EVA283 and 20% EVA220 by mass percentage; (β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) is 1 part of pentaerythritol ester, anti-copper agent is 1 part of hydroxyl-terminated polybutadiene acrylonitrile liquid rubber, rare earth composite stabilizer (REC - 2 parts of LS-D or REC-LS-F), 3 parts of zinc borate as a smoke suppressant, 1 part of trimethylolpropane as a sensitizing cross-linking auxiliary agent, and the balance is paraffin;

[0042] A preparation method of a single-wall heat-shrinkable tube,

[0043] A. Preparation of wall materials:

[0044]The wall material is composed of 80 parts of polyolefin mixed re...

Embodiment 3

[0053] A single-wall heat-shrinkable tube is composed of a wall material. According to the mass parts, the wall material is composed of 80 parts of polyolefin mixed resin and 20 parts of auxiliary agent;

[0054] The polyolefin mixed resin is a polyolefin mixed resin prepared by melt blending four kinds of polyolefin materials of 30% EVA630, 20% EVA421, 40% EVA283 and 10% EVA220 by mass percentage; (β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) is 1 part of pentaerythritol ester, anti-copper agent is 1 part of hydroxyl-terminated polybutadiene acrylonitrile liquid rubber, rare earth composite stabilizer (REC - 2 parts of LS-D or REC-LS-F), 3 parts of zinc borate as a smoke suppressant, 1 part of trimethylolpropane as a sensitizing cross-linking auxiliary agent, and the balance is paraffin;

[0055] A preparation method of a single-wall heat-shrinkable tube,

[0056] A. Preparation of wall materials:

[0057] The wall material is composed of 80 parts of polyolefin mixed r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-shrinkable tube, in particular to a single-wall heat-shrinkable tube and a preparation method thereof. The single-wall heat-shrinkable tube is made from wall materials which comprise 80 parts by weight of polyolefin mixed resin and 20 parts by weight of addition agents. The preparation method comprises the following steps of: preparing the wall materials of the single-wall heat-shrinkable tube; extruding; irradiating; and expanding for forming. Compared with the traditional heat-shrinkable tube, the invention has the technical advantages of keeping the characteristics, i.e. good electrical property, chemical property, and the like of a common heat-shrinkable tube at an outer layer and having all the service properties of the common heat-shrinkable tube and waterproof property, sealing property, dampproof property, anticorrosion property, and the like.

Description

1. Technical field: [0001] The invention relates to a heat-shrinkable tube, in particular to a single-wall heat-shrinkable tube and a preparation method thereof. 2. Background technology [0002] From the birth of heat shrinkable products to the present, the development speed can be said to be rapid, and the application field has been continuously expanded. At the beginning of the production of heat shrinkable products, they were mainly used for insulation protection, and now they are widely used in aviation, aerospace, ships, automobiles, home appliances, communications and petroleum. Chemical industry and other fields. Heat-shrinkable products play the role of sealing moisture-proof, waterproof, anti-corrosion and anti-vibration dislocation for cable joints and branches. Therefore, heat-shrinkable tubes are required to have good physical and electrical properties, such as wear resistance, anti-corrosion Impact resistance, high dielectric strength and other properties; at ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L9/02C08K13/02C08K5/01C08K5/134C08K3/38C08K5/053B29C69/02B29C71/04B29B9/00B29C47/92B29C61/02H02G15/18B29C48/92
CPCB29C48/09
Inventor 张志强庄向阳
Owner 江苏达胜热缩防护用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com