Crystal jade-like ceramic and production method thereof

A technology of jade porcelain and products, applied in the field of jade porcelain and its production, to achieve the effects of improving uniformity, reducing molding defects, improving transparency and moistening effect

Inactive Publication Date: 2012-05-30
中国轻工业陶瓷研究所
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there are limitations in the production of high-end boutique display gift porcelain and decorative ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of jade porcelain, the weight part component of its synthetic composite matrix ceramic material: MgO 2 23.00, Al 2 o 3 67.00, BaO 3.50, SrO 2.00, CaO 3.00, Li 2 O 1.50.

[0016] The above-mentioned synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as the main raw materials for batching, which is the following components in parts by weight: MgO 2 21.00, Al 2 o 3 60.20, BaO 5.30, SrO 1.90, CaO4.30, Li 2 O 1.20, La 2 o 3 1.40, Y 2 o 3 1.90, ZnO 2.80.

[0017] The production technology of described a kind of bright jade porcelain is the following steps:

[0018] First, the composite matrix ceramic material is synthesized, and then the synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as raw materials to make slurry, and then sol-gel injection molding, drying, trimming, firing, Surface polishing, inspection, product.

[0019] The synthesis process of the s...

Embodiment 2

[0029] A kind of jade porcelain, the weight part component of its synthetic composite matrix ceramic material: MgO 2 20.00, Al 2 o 3 71.00, BaO 1.50, SrO 3.20, CaO 2.00, Li 2 O 2.30.

[0030] The above-mentioned synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as the main raw materials for batching, which is the following components in parts by weight: MgO 2 18.60, Al 2 o 3 66.00, BaO 3.80, SrO 2.70, CaO2.70, Li 2 O 2.00, TiO 2 0.50, Y 2 o 3 1.20, La 2 o 3 0.40, ZnO 2.10.

[0031] The production technology of described a kind of bright jade porcelain is the following steps:

[0032] First, the composite matrix ceramic material is synthesized, and then the synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as raw materials to make pulp, and then sol-gel injection molding, drying, trimming, firing, Surface polishing, inspection, product.

[0033] The synthesis proc...

Embodiment 3

[0043] A kind of jade porcelain, the weight part component of its synthetic composite matrix ceramic material: MgO 2 24.60, Al 2 o 3 68.30, BaO 1.40, SrO 1.50, CaO 1.60, Li 2 O 2.60.

[0044] The above-mentioned synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as the main raw materials for batching, which is the following components in parts by weight: MgO 2 21.60, Al 2 o 3 60.70, BaO 3.30, SrO 1.40, CaO3.80, Li 2 O 2.40, Y 2 o 3 2.10, La 2 o 3 1.30, ZnO 3.40.

[0045] The production technology of described a kind of bright jade porcelain is the following steps:

[0046] First, the composite matrix ceramic material is synthesized, and then the synthetic material and calcium, titanium, lanthanum, yttrium, zinc, and barium additives are used as raw materials to make pulp, and then sol-gel injection molding, drying, trimming, firing, Surface polishing, inspection, product.

[0047] The synthesis process of the syn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
glossaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a crystal jade-like ceramic and a production method thereof. Firstly, magnesium, aluminum, barium, strontium, calcium and lithium serving as main components are synthesized into a composite base ceramic material; and then, the composite material and additive are used as raw materials and are prepared into the crystal, smooth and jade-like ceramic with high strength and highhardness by adopting the production processes such as sol-gel injection molding and surface polishing process and the like.

Description

technical field [0001] The invention belongs to the technical field of inorganic non-metallic ceramic materials and product manufacturing thereof, and in particular relates to a jade porcelain and a production method thereof. Background technique [0002] In recent years, foreign display gift porcelain has developed rapidly, with many types of materials and designs and colors, especially the development of high-end boutique products is very good, not only in appearance decoration, but also in porcelain materials, breaking through the limitations of traditional porcelain materials With the use of high-tech ceramic materials, the displayed products not only have a very beautiful appearance but also have good internal performance, which broadens the application range of display gift porcelain and creates good economic and social benefits. In recent years, my country's consumption of high-end consumer goods has accounted for 25% of the global market, surpassing the United States...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/10C04B35/622
Inventor 李亚萍
Owner 中国轻工业陶瓷研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap