Inorganic wooden building board and production method thereof

A building board and inorganic technology, applied in the field of building wood boards and inorganic wood building boards, can solve the problems of the destruction of the earth's ecological environment, shortage of forest resources, consumption of natural wood, etc., achieve good environmental protection performance, protect forest resources, and facilitate construction Effect

Inactive Publication Date: 2010-06-23
沈阳有色冶金设计研究院有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, forest resources in our country are limited resources. Due to a large number of deforestation, the ecological environment of the earth is being severely punished. So far, there has been a shortage of forest resources in many areas. This has also led to the continuous deterioration of some ecological environments.
At present, the raw materials of some existing artificial woods are basically wood, such as fiberboard, particle board, blockboard and other boards, which still need to consume a large amount of natural wood while making it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] An inorganic wood building board is composed of the following components in parts by weight:

[0039] fiberglass: 10;

[0040] Talc powder: 10;

[0041] Kaolin: 10;

[0042] expanded perlite: 5;

[0043] lime powder 10;

[0044] Magnesite 55.

[0045] The preparation method is to grind the above-mentioned components into 40-mesh powder by taking 10 parts of glass fiber, 10 parts of kaolin, 5 parts of expanded perlite and 55 parts of magnesite according to the ratio of parts by weight, and then Take 10 parts of talcum powder and 10 parts of lime powder and mix evenly to make a plate. From the outer layer to the inner layer, the plate is a wear-resistant outer layer, an inorganic raw material layer, and a wear-resistant bottom layer.

Embodiment 2

[0047] An inorganic wood building board is composed of the following components in parts by weight:

[0048] fiberglass: 5;

[0049] Talc: 5;

[0050] Kaolin: 20;

[0051] expanded perlite: 5;

[0052] lime powder 25;

[0053] Magnesite 40.

[0054] The preparation method is to grind the above-mentioned components into 100-mesh powder by taking 5 parts of glass fiber, 20 parts of kaolin, 5 parts of expanded perlite and 10 parts of magnesite according to the ratio of parts by weight, and then Take 5 parts of talcum powder and 25 parts of lime powder and mix evenly to make a plate. From the outer layer to the inner layer, the plate is a wear-resistant outer layer, an inorganic raw material layer, and a wear-resistant bottom layer.

Embodiment 3

[0056] The described inorganic wood building board is composed of the following components in parts by weight:

[0057] fiberglass: 10;

[0058] Talc powder: 10;

[0059] Kaolin: 30;

[0060] expanded perlite: 10;

[0061] lime powder 10;

[0062] Magnesite 30.

[0063] The preparation method is to take 10 parts of glass fiber, 30 parts of kaolin, 10 parts of expanded perlite and 30 parts of magnesite according to the ratio of parts by weight of each component, and grind them into 200 mesh powder, and then press the above-mentioned Proportion Take 10 parts of talcum powder and 10 parts of lime powder and mix evenly to make a plate. From the outer layer to the inner layer, the plate is a wear-resistant outer layer, an inorganic raw material layer, and a wear-resistant bottom layer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building materials, in particular to an inorganic wooden building board which can substitute the existing building wood sheet. The invention provides a novel building board which integrates the functions of fire prevention, watertight and anticorrosion into a whole, has beautiful appearance, is similar to the natural timber, can eradicate the drawback that people continuously cut the natural timber to be used as building materials, and plays an excellent protection role of maintaining the ecological balance of the human being. The inorganic wooden building board has the characteristics of fire proofing, water proofing, anticorrosion and rust protection, being difficult to age and deform and the like, simultaneously can prevent damage caused by worms, and is a good substitute of the natural timber resources. The product of the invention has wide application range, low price, convenient construction, sufficient raw materials and good market application prospect, not only can better protect the forest resources of China, but also satisfies the requirements of the construction industry. The inorganic wooden building board has very good environmental performance, convenient drawing of materials, and thereby being very suitable to be promoted and applied, and having extremely wide economic benefit and social benefit.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an inorganic wood building board, which can replace the existing building wood board. Background technique [0002] At present, due to the continuous development of the construction industry, people build a large number of various houses, which requires a large amount of wood. However, forest resources in our country are limited resources. Due to a large number of deforestation, the ecological environment of the earth is being severely punished. So far, there has been a shortage of forest resources in many areas. It has also caused the continuous deterioration of some ecological environments. And the raw material of some existing artificial woods is also to use wood substantially at present, such as boards such as fiberboard, particle board, blockboard, and it still needs to consume a large amount of natural woods when making. For this reason, people need to find a b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/30C04B14/42C04B14/10C04B14/18
CPCC04B2111/20C04B2111/28C04B2111/27C04B2111/26C04B2111/00017C04B28/10C04B2111/00612
Inventor 李哲
Owner 沈阳有色冶金设计研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products