Special card sheet for laser printer and preparation method thereof

A technology of laser printers and special certificates, which is applied to information-carrying cards, printing, printed matter, etc., can solve the problems of complex production process, inability to adapt to on-site certificate production, and long time for card production, so as to achieve simple production process and shorten card production time and reduce the cost of card making

Active Publication Date: 2011-08-03
TIANJIN BOYUAN NEW MATERIALS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Disclosed in Chinese patent document CN1304837A (disclosure date is 2001.07.25) a kind of making technology that utilizes laser printing-laminated color personality card, this card making technology utilizes laser printer to improve the definition of making card, but this patent is in When making cards, it is first necessary to use a laser printer to print, add lining, and then laminate and punch the card to prepare the shape. The manufacturing process is very complicated and the card making time is long, which cannot meet the needs of on-site card making

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special card sheet for laser printer and preparation method thereof
  • Special card sheet for laser printer and preparation method thereof
  • Special card sheet for laser printer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] A method for preparing a card material dedicated to a laser printer, comprising the steps of:

[0020] (1) Preparation of adhesive solution: Add deionized water and ethanol with a weight ratio of 1:2 into a stainless steel bucket, stir evenly, then put in adhesive, continue stirring for 1 hour, start to heat up to 40°C and maintain 1 hour, then down to room temperature, the binder solution was obtained;

[0021] (2) Preparation of pigment slurry: adding the inorganic pigment and dispersant to the mixed solution of deionized water and ethanol with a weight ratio of 1:3, stirring, pre-dispersing and shearing dispersion, to prepare the pigment slurry;

[0022] (3) Prepare the toner receiving layer coating solution: mix the binder solution and the pigment slurry, add a curing agent and a wetting agent to prepare the toner receiving layer coating solution;

[0023] (4) Coating the toner-receiving layer coating solution on the upper surface of the film base, the coating meth...

Embodiment 1

[0026] Sheet base selects PET white sheet base for use, and each component of the toner receiving layer coated on its surface and the parts by weight of each component are as follows:

[0027]

[0028]

[0029] The preparation process of the special card material for laser printers is as follows:

[0030] 1. Prepare adhesive solution: Weigh 15.9 parts of deionized water and 31.8 parts of ethanol, add them into a stainless steel bucket, stir evenly, then put 5.3 parts of PVB into it while stirring, continue stirring for 1 hour, and start to heat up to 40°C and maintained for 1 hour, then lowered to room temperature to obtain PVB solution (adhesive solution);

[0031] 2. Preparation of pigment slurry: according to the formula, add the remaining amount of deionized water (5.3 parts) and the remaining amount of ethanol (15.9 parts) into a stainless steel bucket, add 0.053 parts of acetic acid, stir well, add 5.3 parts of pseudo thin water Aluminum stone, continue to stir an...

Embodiment 2

[0035] Sheet base selects PET white sheet base for use, and each component of the toner receiving layer coated on its surface and the parts by weight of each component are as follows:

[0036]

[0037] The preparation process of the special card material for laser printers is as follows:

[0038] 1. Preparation of adhesive solution: Weigh 15.9 parts of deionized water and 31.8 parts of ethanol, add them into a stainless steel bucket, stir evenly, then put 5.3 parts of PVB into it under stirring, continue stirring for 1 hour, and start to heat up to Maintain at 40°C for 1 hour, then drop to room temperature to obtain PVB solution (adhesive solution);

[0039] 2. Preparation of pigment slurry: according to the formula, add the remaining amount of deionized water (79.5 parts) and the remaining amount of ethanol (238.5 parts) into a stainless steel bucket, add 1.6 parts of acetic acid, stir well, add 79.5 parts of pseudo thin water Aluminum stone, continue to stir and pre-disp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a special card sheet for a laser printer and a preparation method thereof. The special card sheet for the laser printer consists of a film base and a toner receiving layer, wherein the toner receiving layer is coated at the upper surface of the film base, the toner receiving layer is technically characterized by comprising an inorganic pigment and an adhesive according tothe weight ratio of 1:1-15:1, and the coating amount of the toner receiving layer is 5-25 g / m<2> based on dry weight. In the preparation method, coating liquid of the toner receiving layer is firstlyprepared and then is coated at the upper surface of the film base by using an extrusion coating mode. The invention has reasonable design and adopts the laser printer to directly print and form an image on the card sheet, greatly shortens the card-making time, reduces the card-making cost, enhances the card-making precision, improves the water-proofness, the wear resistance and the service life of the card and can be widely used for making various cards on site and making various personalized cards.

Description

technical field [0001] The invention belongs to the field of card making materials, in particular to a special card material for laser printers and a preparation method thereof. Background technique [0002] With the advent of the information age, there are more and more applications of various information recording materials, and cards have been widely used as a typical representative of information recording carriers. At present, the production of personalized cards (such as: PVC color portrait cards such as work permits, student permits, examination admission permits, temporary residence permits, driver's licenses, etc.) is mainly made of traditional inkjet printing materials. Due to problems such as poor performance, the service life of the card has been greatly limited. People are constantly looking for simple and fast ways to make certificates to adapt to the fast-changing information environment, and there are more and more requirements for on-site and personalized c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L29/14C08L67/08C08L1/02C08K3/36B42D15/10C08L89/00C08L39/06C08K3/26B41M5/52C08L31/04B42D25/20
Inventor 李春刚鹿秀山孙鹏李维苏景丽刘柏松
Owner TIANJIN BOYUAN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com