Grease special for plastic and preparation method thereof
A grease and plastic technology, applied in the field of plastic grease, can solve the problems of lack of protection and poor high temperature resistance of plastic materials, and achieve the effect of stable colloidal stability and strong high temperature resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Example 1: A special grease for plastics, the preparation steps are as follows:
[0034] 1. Add 40kg of polydimethylsiloxane with a polymerization viscosity of 50mPa.s at 25°C and 10kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir evenly.
[0035] 2. Add 1kg polytetrafluoroethylene, 0.5kg 2,6-di-tert-butyl-p-cresol, 0.5kg ethylene glycol, and stir well.
[0036] 3. Add 6kg and the specific surface area is 230m 2 / g The dehydrated hydrophobic silica treated by chlorosilane, stir well.
[0037] 4. Heat the reactor to 140°C and stir for 2 hours to form the base material.
[0038] 5. Grind the base material twice with a three-roll mill to form fat.
[0039] 6. Defoaming the obtained grease, vacuum for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stop the vacuum, and fill the tank.
Example Embodiment
[0040] Example 2: A special grease for plastics, the preparation steps are as follows:
[0041] 1. Add 70kg of polydibutylsiloxane with a polymerization viscosity of 20000mPa.s at 25°C and 40kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir well.
[0042] 2. Add 3kg of polytetrafluoroethylene, 1kg of 4,4'-thiobis(3-methyl-6-tert-butyl)phenol, 2kg of polyethylene glycol, and stir well.
[0043] 3. Add 14kg and the specific surface area is 230m 2 / g The dehydrated hydrophobic silica treated by chlorosilane, stir well.
[0044] 4. Heat the reactor to 140°C and stir for 2 hours to form the base material.
[0045] 5. Grind the base material twice with a three-roll mill to form fat.
[0046] 6. Defoaming the grease obtained, vacuuming for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stopping the vacuum, and filling the tank.
Example Embodiment
[0047] Example 3: A special grease for plastics, the preparation steps are as follows:
[0048] 1. Add 40kg of polymethylvinylsiloxane with a polymerization viscosity of 2000mPa.s at 25°C and 40kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir well.
[0049] 2. Add 2kg of molybdenum disulfide, 0.75kg of 2,6-di-tert-butyl-p-cresol, and 1kg of glycerin and stir well.
[0050] 3. Add 10kg and the specific surface area is 230m 2 / g The dehydrated hydrophobic white carbon black treated with silazane, stir evenly.
[0051] 4. Heat the reaction kettle to 140°C and stir for 2 hours to form the base material.
[0052] 5. Grind the base material twice with a three-roll mill to form fat.
[0053] 6. Defoaming the obtained grease, vacuum for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stop the vacuum, and fill the tank.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap