Preparation method of mesoporous silicon oxide-based silver catalyst and application thereof in carbon monoxide oxidation

A catalyst and mesoporous technology, which is applied in the field of inorganic nano-catalytic materials, can solve the problems such as the unsatisfactory CO oxidation and purification effect, and achieve good industrial application prospects, high catalytic CO low-temperature catalytic activity, and convenient operation.

Inactive Publication Date: 2010-11-24
DALIAN UNIV OF TECH
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Silver is relatively cheap, but it is not very effective for CO oxidation purification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of mesoporous silicon oxide-based silver catalyst and application thereof in carbon monoxide oxidation
  • Preparation method of mesoporous silicon oxide-based silver catalyst and application thereof in carbon monoxide oxidation
  • Preparation method of mesoporous silicon oxide-based silver catalyst and application thereof in carbon monoxide oxidation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Add 1.25g of dodecylamine to 10ml of absolute ethanol, stir in a water bath at 25°C, and completely dissolve the dodecylamine until a transparent solution is formed. Add 5ml tetraethyl orthosilicate to the solution, stir for 2h, then add 10ml deionized water to the solution, stir for 1h, then add 0.2ml formaldehyde solution to the solution, stir for 0.5h, then add 0.085g silver nitrate to the solution , The reaction was stirred continuously for 24h. Wash with deionized water, filter, dry in an oven at 100°C for 12h, and calcinate in a muffle furnace at 450°C for 4h in an air atmosphere to obtain Ag / SiO 2 catalyst. Its XRD, N 2 Adsorption-desorption and pore size distribution such as figure 1 , as shown in 2, 3.

[0027] The activity evaluation of the catalyst was carried out in a fixed-bed continuous flow differential reactor, the reactor was a glass U-shaped tube with an inner diameter of 4mm, the catalyst loading was 200mg, and the feed gas composition: 1% CO (vol...

Embodiment 2

[0029] According to the preparation method of the present invention in Example 1, the order of reagent addition is changed, followed by silver nitrate, water, tetraethyl orthosilicate, and formaldehyde, see Catalytic Activity Figure 4 .

Embodiment 3

[0031] According to the preparation method of the present invention in Example 1, the order of adding reagents is changed, followed by formaldehyde, silver nitrate, water, and tetraethyl orthosilicate, and the catalytic activity is shown in Figure 4 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a mesoporous SiO2-based Ag catalyst and application thereof in CO oxidation. The method is characterized by comprising the following steps: preparing an Ag / SiO2 catalyst by a one-step method by using lauryl amine as a template agent; dissolving the lauryl amine in absolute ethyl alcohol, vigorously stirring in a water bath kettle at a certain temperature to enable the lauryl amine to be completely dissolved; adding silicon sources, de-ionized water, formaldehyde and silver nitrate according to a certain ratio, sequence and time interval, continuing stirring for a period of time, washing with de-ionized water, leaching, drying, and calcining to obtain the Ag / SiO2 catalyst with a mesoporous structure; and using the Ag / SiO2 catalyst in a CO low-temperature catalytic oxidation reaction. The preparation method can prepare the Ag / SiO2 catalyst with a mesoporous structure and a high specific surface area, and the prepared Ag / SiO2 catalyst has high CO low-temperature oxidation catalysis activity and huge application prospects.

Description

technical field [0001] The invention relates to a mesoporous SiO 2 The invention discloses an Ag-based catalyst and a preparation method thereof, and applies it to catalyze the low-temperature oxidation of CO, belonging to the field of inorganic nano-catalytic materials. Background technique [0002] CO is one of the main pollutants in the air of many industrial environments and indoor environments, especially in fierce battlefields, fire scenes, mine tunnels and other occasions, it is a deadly poison. Therefore, the elimination of CO has extremely important practical significance for the environment and industrial production, and catalytic oxidation is a simple, cheap and effective method. So far, people have mostly studied the use of noble metal catalysts such as Pt, Rh, and Au to catalyze CO oxidation. However, its wide application in industry is limited due to its high price and easy deactivation. [0003] Silver is relatively cheap, but it is not very effective for C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/50B01D53/86B01D53/62
CPCY02A50/20
Inventor 曲振平张晓东贾静璇李新勇
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com