Water-based transparent anticorrosive paint, preparation method and application method thereof

An anti-corrosion coating and transparent technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as product returns or fines, environmental pollution, and health effects of operators, achieving strong adhesion and rust prevention. good effect

Inactive Publication Date: 2010-12-01
资阳赛特化工有限公司
View PDF3 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of them are painted with solvent-based coatings. Solvent-based coatings contain a large amount of organic solvents, which pollute the environment and have a serious impact on the health of operators. Moreover, there are environmental protection problems when products are exported, resulting in product returns or Remaining issues such as fines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of above-mentioned water-based transparent anticorrosion coating comprises the steps: A, the preparation of emulsifier: carry out with bisphenol A type epoxy resin and Polyethylene Glycol according to the mol ratio of epoxy group and hydroxyl be the ratio of 1: 1 After mixing, put it into a flask with a stirring device, heat up to 80-90°C to melt the raw materials, stir and mix evenly, add the catalyst boron trifluoride etherate complex dropwise in a proportion of 0.005%-0.03% of the total amount of materials, at 80 React at ~90°C for 1 hour, discharge the material, cool at room temperature to obtain a polymer emulsifier, and then follow the formula of polymer emulsifier: benzylphenol polyoxyethylene ether formaldehyde condensate: phenol formaldehyde condensate sulfonic acid sodium salt = 2:1 : 1 ratio mixes and makes epoxy resin emulsifier; B, the preparation of epoxy resin emulsion: utilize the method for high-speed dispersion, epoxy resin is emu...

Embodiment 1

[0042] The formula used to prepare the water-based transparent anti-corrosion paint is: 30% epoxy resin emulsion; 50% transparent anti-rust pigment; 3% auxiliary agent; 17% water. Among them, the main components of the transparent antirust pigment are aluminum dihydrogen phosphate and aluminum tripolyphosphate; the epoxy resin emulsion is an epoxy emulsion obtained after emulsifying with bisphenol A epoxy resin; the auxiliary agents are dispersants and defoamers , Anti-flash rust agent, leveling agent, anti-settling agent, anti-fungal agent and thickener.

[0043]The preparation method of water-based transparent anticorrosion coating: A, the preparation of emulsifier: bisphenol A type epoxy resin and Polyethylene Glycol are mixed according to the mol ratio of epoxy group and hydroxyl and then add the ratio of 1: 1 with In the flask of the stirring device, heat up to 80°C to melt the raw materials, stir and mix evenly, add the catalyst boron trifluoride etherate complex dropwis...

Embodiment 2

[0047] The formula used to prepare the water-based transparent anticorrosion paint is: 40% epoxy resin emulsion; 35% transparent antirust pigment; 5% additive; 20% water. Among them, the main component of the transparent anti-rust pigment is aluminum tripolyphosphate; the epoxy resin emulsion is an epoxy emulsion obtained after emulsifying with bisphenol A epoxy resin; the auxiliary agents are dispersant, defoamer, anti-flash rust agent , leveling agent, anti-settling agent, anti-fungal agent and thickener.

[0048] The preparation method of water-based transparent anticorrosion coating: A, the preparation of emulsifier: bisphenol A type epoxy resin and Polyethylene Glycol are mixed according to the mol ratio of epoxy group and hydroxyl and then add the ratio of 1: 1 with In the flask of the stirring device, heat up to 90°C to melt the raw materials, stir and mix evenly, add the catalyst boron trifluoride etherate complex dropwise in a proportion of 0.005% of the total amount ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based transparent anticorrosive paint, a preparation method and an application method thereof. The preparation method thereof comprises the following steps: firstly, utilizing an emulsifier to emulsify epoxy resin into an epoxy resin micro-fine emulsion; then adding various auxiliaries, rust-proofing pigments and water, and utilizing a high-speed disperser to evenly disperse the mixture; and finally grinding the dispersed mixture into the water-based transparent anticorrosive paint with the fineness less than 30 mu m by utilizing a sand mill. The application method thereof comprises: adding a water-based epoxy hardener into the water-based transparent anticorrosive paint in the mass ratio of 2:1. The water-based transparent anticorrosive paint is matched with the water-based epoxy hardener for use; and after being covered on ferrous metal, being subjected to chemical reaction and being crosslinked to form a film, the water-based transparent anticorrosive paint has strong adhesive force, good rust prevention, water resistance, oil resistance and other performances, and can maintain the primary color of metal.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a water-based transparent anticorrosion paint and its preparation and application method. technical background [0002] my country is a big steel country and also a big country that produces seamless steel pipes. Many seamless steel pipes are exported to other countries and regions. Since the seamless steel pipe is easy to oxidize and rust in the natural state, it has a lot of influence on its appearance and quality. The strength has a great influence, and the anti-corrosion treatment of seamless steel pipes includes phosphating, passivation, coating, etc., of which coating accounts for a large proportion. At present, most of them are painted with solvent-based coatings. Solvent-based coatings contain a large amount of organic solvents, which pollute the environment and have a serious impact on the health of operators. Moreover, there are environmental protection probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D7/12C09D5/08
Inventor 施国全
Owner 资阳赛特化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com