Polycarbonate combination and preparation method thereof

A technology of polycarbonate and composition, applied in the field of polycarbonate composition and its preparation, can solve the problems of difficult to achieve flame retardancy, decreased light transmittance, uneven dispersion of flame retardant and light diffusing agent, etc. The effect of high rate, excellent light diffusion performance and excellent flame retardant performance

Inactive Publication Date: 2010-12-08
SINOPLAST NEW MATERIAL
View PDF4 Cites 51 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, on the one hand, organophosphorus flame retardants are easy to precipitate during injection molding and extrusion, which has a great influence on the mechanical properties and light transmittance of the product. The flammability is difficult to reach the UL94 standard V-0 level under 1.6mm, and although increasing the addition amount can further improve the flame retardancy of the material, it will also make the light transmittance drop more seriously. At the same time, due to the flame retardant and light diffusion in the finished product Inhomogeneous dispersion of the agent is prone to white spot defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarbonate combination and preparation method thereof
  • Polycarbonate combination and preparation method thereof
  • Polycarbonate combination and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] According to the preparation method of polycarbonate composition of the present invention, comprises steps:

[0034] Weigh each component raw material of aforementioned polycarbonate composition;

[0035] Put the weighed raw materials of each component into the mixer and mix evenly;

[0036] The uniformly mixed raw materials are melted, kneaded, extruded and granulated through an eight-temperature zone twin-screw extruder, and the residence time of the compound in the extruder is controlled at 1 to 2 minutes. The temperature control of the twin-screw extruder is: 260-270°C in zone 1, 270-290°C in zone 2, 270-290°C in zone 3, 270-290°C in zone 4, 270-290°C in zone 5 , Zone 6 is 270-290°C, Zone 7 is 270-290°C, Zone 8 is 270-290°C, head temperature is 250-280°C, and melt temperature is controlled at 260-285°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a polycarbonate combination and a preparation method thereof. In terms of 100 parts of polycarbonate materials by weight, the polycarbonate combination comprises the following components in parts by weight: 100 parts of polycarbonate, 1-10 parts of copolyester, 0.01-0.5 part of aromatic sulphosalts fire retardant, 0.05-0.35 part of organic silicon fire retardant, 0.05-5 parts of anti-dripping agent, 1-15 parts of photodiffusion agent master batches and 0.05-5 parts of antioxidant. The preparation method of the polycarbonate combination comprises the following steps: adding the components of the polycarbonate combination as required into a blender mixer, and evenly stirring and mixing; and carrying out melt mixing, extrusion and granulation on the evenly mixed raw materials in eight temperature areas of a double-screw extruder. The polycarbonate combination provided by the invention has excellent photodiffusion performance, high light transmittance, excellent flame retardant property, safety, environmental protection, favorable heat resistance, easy molding and reduced crystal point defect.

Description

technical field [0001] The invention relates to a polycarbonate composition and a preparation method thereof, in particular to a polycarbonate composition improved in terms of light diffusion, flame retardancy, transparency, moldability, product crystal point defects, and safety and environmental protection. its preparation method. Background technique [0002] Polycarbonate (PC) is a widely used engineering plastic with excellent mechanical properties, heat resistance and weather resistance, etc., and has high light transmittance. Therefore, it has been widely used in heat resistance and moisture absorption than acrylic resin. Polycarbonate with better performance is used as the matrix resin of the light diffuser plate. [0003] However, there are currently increasingly higher performance requirements for plastic materials used in light boxes, lampshades and backlight panels, especially with the development of LED technology. For example, it is required that it must have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L83/04C08K5/42C08K3/30C08K3/26C08K3/34B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895
Inventor 朱怀才
Owner SINOPLAST NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products