Aqueous PU (Polyurethane) dry slippery feel treated agent for synthetic leather

A synthetic leather and treatment agent technology, which is applied in fiber treatment, textiles and papermaking, etc., can solve the problems of poor viscosity, stability, hand touch, poor hand feeling of synthetic leather, and dissolution of the bottom layer of synthetic leather, etc., to achieve comprehensive Excellent effect, low cost, and solvent-resistant coating

Inactive Publication Date: 2010-12-29
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]1. The organic solvent contained in the solvent-based dry-slip surface treatment agent will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good ;
[0005]2. The organic solvent contained in the solvent-based dry-slip surface treatment agent not only has high cost, strong smell, and is easy to pollute the environment, but also has flammable and explosive substances. other safety hazards;
[0006]3. Synthetic leather products prepared by solvent-based dry-slip surface treatment agents have poor comprehensive effects such as viscosity, stability, and hand feeling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1. The water-based PU dry slip treatment agent for synthetic leather is composed of the following raw materials: 100 kg of water-based polyurethane resin (30% solid content), 150 kg of tap water, 4 kg of modified silicone polymer, 15 kg of modified amino silicone oil, 2 kg of water-based polyurethane thickener, 0.8 kg of silicone defoamer, and 1.5 kg of silicone leveling agent.

[0029] 2. The preparation method of the water-based PU dry slippery treatment agent for synthetic leather of the present invention is as follows:

[0030] ① Proportionally select 100 kg of water-based polyurethane resin (30% solid content), 4 kg of modified silicone polymer, 15 kg of modified amino silicone oil, 1.5 kg of silicone leveling agent, 0.8 kg of silicone defoamer and 150 kg of tap water kg, mixed and stirred for 2 to 3 hours, fully mixed and set aside;

[0031] ② Grinding and filtering the reaction mixture obtained in step ①;

[0032] 3. Take the mixture obtained by step 2. filter,...

Embodiment 2

[0037] 1. The water-based PU dry slip treatment agent for synthetic leather consists of the following raw materials: 80 kg of aliphatic polyurethane emulsion (30% solid content), 120 kg of tap water, 6 kg of silicone-acrylate copolymer emulsion, and 14 kg of modified amino silicone oil. kg, 4 kg of water-based polyurethane thickener, 5 kg of silicone defoamer, and 2 kg of silicone leveling agent.

[0038] 2. The preparation method of the water-based PU dry slippery treatment agent for synthetic leather of the present invention is as follows:

[0039] ① Proportionally select 80 kg of aliphatic polyurethane emulsion (30% solid content), 6 kg of silicone-acrylate copolymer emulsion, 14 kg of modified amino silicone oil, 2 kg of silicone leveling agent, 5 kg of silicone defoamer and 120 kg of tap water, mixed and stirred for 2 to 3 hours, fully mixed and set aside;

[0040] ② Grinding and filtering the reaction mixture obtained in step ①;

[0041] 3. Take the mixture obtained by...

Embodiment 3

[0046] 1. The water-based PU dry slip treatment agent for synthetic leather consists of the following raw materials: 60 kg of aromatic polyurethane emulsion (30% solid content), 100 kg of tap water, 2 kg of silicone modified epoxy resin, and modified amino silicone oil 10 kg, 1 kg of non-ionic polyurethane polymer, 4 kg of silicone defoamer, 1 kg of silicone leveling agent.

[0047] 2. The preparation method of the water-based PU dry slippery treatment agent for synthetic leather of the present invention is as follows:

[0048]① Proportionally select 60 kg of aromatic polyurethane emulsion (30% solid content), 2 kg of silicone modified epoxy resin, 10 kg of modified amino silicone oil, 1 kg of silicone leveling agent, and 4 kg of silicone defoamer and 100 kg of tap water, mix and stir for 2 to 3 hours, fully mix, and set aside;

[0049] ② Grinding and filtering the reaction mixture obtained in step ①;

[0050] ③ Take the mixture obtained in step ② and filter, add 1 kg of non...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous PU (Polyurethane) dry slippery feel treated agent for synthetic leather, which comprises the following raw materials in percentage by weight: 30-40 percent of aqueous PU resin, 50-60 percent of water, 1-3 percent of modified organosilicon polymer, 5-7 percent of modified amino silicone oil, 0.5-1 percent of organosilicon flatting agent, 2-5 percent of organosilicon defoaming agent and 0.5-2 percent of aqueous PU thickening agent. The aqueous PU (Polyurethane) dry slippery feel treated agent for the synthetic leather has the advantages of scientific and reasonable proportion of all the components, coordination and combined action of the components, good film forming, firm bonding, solvent resistance of a coating, cold resistance, hydrolysis resistance, heat resistance and anti-aging; and particularly, the combined action of the modified organosilicon polymer and the modified amino silicone oil ensures that the dry slippery feel of treated leather is unique, and the synthetic leather has good combined effect in the aspects of feeling, waterproofing, bonding, and the like.

Description

technical field [0001] The invention relates to a dry-slip surface treatment agent for synthetic leather, in particular to a water-based PU dry-slip surface treatment agent for synthetic leather used in the back-stage process of synthetic leather. Background technique [0002] With the improvement of people's living standards, people are gradually pursuing high-quality daily products, and the demand for leather products is increasing. With the enhancement of animal protection awareness, animal leather can no longer meet people's needs. At present, synthetic leather products have gradually become a popular trend in the future. Synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is canvas PU material with good tensile strength. In addition to being coated on the base fabric In addition to the upper surface, the base fabric can also be included in the middle, so that the existence of the base ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/564D06M15/643D06M15/55D06M15/53D06M15/256D06M11/50
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com