A metal material and anti-carburization technology, which is applied in the field of metal materials, can solve the problems that C solid solution strengthening cannot be expected, and high-temperature strength cannot be obtained, so as to improve durability and operating efficiency, suppress metal dusting, and improve weldability. Effect

Active Publication Date: 2011-01-12
NIPPON STEEL CORP
View PDF16 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the solid-solution strengthening of C cannot be expected, and sufficient high-temperature strength cannot be obtained.
Therefore, it is not suitable as a metal material used at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carburization resistant metal material
  • Carburization resistant metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0122] Metal materials with the chemical compositions shown in Table 1 were melted in a high-frequency heating vacuum furnace, and then hot forged and hot rolled to produce metal plates with a thickness of 6 mm. The metal plate was subjected to solution heat treatment under the condition of 1160 to 1230° C.×5 minutes, and a part of the metal plate was cut to prepare a test piece.

[0123] A test piece having a width of 15 mm x a length of 20 mm was cut out from the metal material described in Table 1. Place the test piece in a volume ratio of 45% CO-42.5% H 2 -6.5%CO 2 -6%H 2 It was kept isothermally at 650° C. in an atmosphere of O gas, and after 200 hours, it was taken out, and whether or not pits were formed on the surface of the test piece was judged visually and by observation with an optical microscope. The results are summarized in Table 2.

[0124]

[0125] [Table 2]

[0126]

[0127] It can be seen from Table 2 that among the metal materials Nos. 24 to 33 w...

Embodiment 2

[0129] Metal materials with the chemical compositions shown in Table 1 were melted in a high-frequency heating vacuum furnace, and then hot forged and hot rolled to produce metal plates with a thickness of 6 mm. The metal plate was subjected to solution heat treatment under the condition of 1160 to 1230° C.×5 minutes, and a part of the metal plate was cut to prepare a test piece. A test piece having a width of 15 mm x a length of 20 mm was cut out from the metal material described in Table 1. Place the test piece at 30%C by volume ratio 3 h 8 -70%H 2 In a gas atmosphere, keep isothermally at 650° C., take it out after 10 hours, and judge whether pits (pits) occur on the surface of the test piece by visual observation and optical microscope observation. The results are summarized in Table 2.

[0130] As can be seen from Table 2, among the metal materials of numbers 24 to 33 whose chemical composition does not fall into the conditions specified in the present invention, the ...

Embodiment 3

[0132] Metal materials with the chemical composition shown in Table 1 were smelted in a high-frequency heating vacuum furnace, and then hot forged and hot rolled to produce two metal plates each with a thickness of 12 mm, a width of 50 mm, and a length of 100 mm. The metal plate was subjected to solution heat treatment under the condition of 1200° C.×5 minutes, and a part of the metal plate was cut to prepare a test piece.

[0133] Next, after performing V-shaped groove processing at an angle of 30° and a root thickness of 1.0mm on one side of the longitudinal direction of the above-mentioned test piece, using "DNiCrMo-3" specified in JIS Z3224 (1999) as an electrode, the thickness of 25mm, A commercially available metal plate of "SM400C" specified in JIS G 3106 (2004) having a width of 150 mm and a length of 150 mm was subjected to restraint welding on the four sides. Then, using "YNiCrMo-3" TIG welding wire specified in JIS Z3334 (1999), multilayer welding was performed in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A metal material which exhibits both excellent workability and excellent metal dusting resistance and which is suitable for use as the material in a cracking furnace, a reforming furnace, a heating furnace, or a heat exchanger in petroleum refining or petrochemical plants or the like. A carburization-resistant metal material characterized by containing by mass C: 0.08 to 0.4%, Si: 0.6 to 2.0%, Mn: 0.05 to 2.5%, P: 0.04% or less, S: 0.015% or less, Cr: 18 to 30%, Ni: 20 to less than 30%, Cu: 0.5 to 10.0%, Al: 0.01 to 1%, Ti: 0.01 to 1%, N: 0.15% or less, O (oxygen): 0.02% or less with the balance consisting of Fe and impurities and by satisfying relationship (1). The material may further contain one or more of Co, Mo, W, B, V, Zr, Nb, Hf, Mg, Ca, Y, La, Ce and Nd. C > 0.062Si + 0.033Cu - 0.004Cr + 0.043 (1) (wherein each symbol of element represents the content of the element in mass%).

Description

technical field [0001] The present invention relates to a metal material with high high-temperature strength and excellent corrosion resistance, which can be used in a carburizing gas atmosphere containing hydrocarbon gas or CO gas, especially as a cracking furnace in petroleum refining or petrochemical equipment, etc. Metal materials excellent in weldability and metal dusting resistance are preferable as raw materials for reforming furnaces, heating furnaces, heat exchangers, and the like. Background technique [0002] Demand for clean energy fuels such as hydrogen, methanol, liquid fuels (GTL: Gas to Liquids), and dimethyl ether (DME) is expected to increase significantly in the future. Therefore, a reformer for producing such a synthesis gas needs to be larger in size, further improved in thermal efficiency, and suitable for mass production. In addition, in order to further improve energy efficiency, in order to further improve energy efficiency, more and more used Heat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/00C22C38/58
CPCC22C38/50C22C38/42C22C38/06C22C38/02C22C38/04C22C38/34C22C38/58
Inventor 西山佳孝小薄孝裕松本聪
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka