Bi-component waterproof paint for roads and bridges and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A waterproof coating, two-component technology, applied in the field of waterproof coatings, can solve the problems of insufficient tensile strength, cold and heat resistance, low shear strength and bonding strength, and unsatisfactory waterproof effect, and achieves good durability. , High bond strength and shear strength, excellent bond strength and shear strength effect
Inactive Publication Date: 2011-02-09
SHANGHAI ORIENTAL YUHONG WATERPROOF TECH
View PDF2 Cites 15 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Cement-based waterproof materials have good durability and are fully compatible with the base surface, but they are not suitable for deformation, and the waterproof effect is not ideal; polymer waterproof materials are adaptable to deformation, but have poor compatibility with the base surface, and have aging problems, and their durability is insufficient
The polymer cement-based waterproof coating prepared by combining the two has made up for the defects of the two materials to a certain extent, but there are still some defects such as insufficient tensile strength, cold and heat resistance, poor aging resistance, and partial shear strength and bonding strength. Low level defects
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] Embodiment 1: by weight, with emulsion 35%, plasticizer 6%, softener 2%, antifreeze agent 3%, preservative 0.5%, thickener 1.5% and water 3% mechanically stir, add 1.5% defoamer, stir until there is no foam, as component A; blend 32% cement, 14% quartz sand and 1.5% wood flour, stir well, and use it as component B; then mix component A with group B Mix evenly and serve.
Embodiment 2
[0026] Embodiment 2: by weight, with emulsion 43%, plasticizer 3%, softener 1%, antifreeze agent 1%, preservative 1%, thickener 2% 1 and water 2.5% mechanical stirring, again Add defoamer %, stir until there is no foam, as component A; blend 28% cement, 17.5% quartz sand and 1% wood flour, stir well, and use it as component B; then mix component A with group B Mix evenly and serve.
Embodiment 3
[0027] Embodiment 3: by weight, with emulsion 29%, plasticizer 0.5%, softening agent 1.5%, antifreeze agent 3%, preservative 1%, thickener 2.5% and 2.5% water mechanically stir, add 2% defoamer, stir until there is no foam, as component A; blend 34% cement, 23.5% quartz sand and 1.5% wood flour, stir well, and use it as component B; then mix component A with group B Mix evenly and serve.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a bi-component waterproof paint for roads and bridges and a preparation method thereof. The waterproof paint comprises 10-70% of emulsion and auxiliary agents as component A and 30-90% of cement, quartz sand as well as wood powder as component B. By weight, the component A comprises 5-50% of emulsion, 0.1-10% of plasticizing agent, 0.1-4% of defoaming agent, 0.1-3% of softening agent, 0.1-4% of antifreeze agent, 0.1-3.5% of thickening agent, 0.1-2% of preservative and the balance of water; and the component B comprises 10-50% of cement, 8-40% of quartz sand and 0.5-5% of wood powder. The invention has the following advantages that the bi-component waterproof paint for roads and bridges is prepared through the synergistic effect of compounding and superposing various materials; and the waterproof paint has great tension strength and excellent ageing resistance, water resistance, heat resistance and cold resistance, and has superior bonding strength and shear strength.
Description
technical field [0001] The invention relates to a waterproof coating, in particular to a two-component waterproof coating for roads and bridges and a preparation method thereof. Background technique [0002] In traditional waterproofing technology, cement is used for rigid waterproofing, and polymer materials are used for flexible waterproofing. Cement-based waterproof materials have good durability and are fully compatible with the base surface, but are not suitable for deformation, and the waterproof effect is not ideal; polymer waterproof materials are adaptable to deformation, but have poor compatibility with the base surface, and have aging problems, and their durability is insufficient. The polymer cement-based waterproof coating prepared by combining the two has made up for the defects of the two materials to a certain extent, but there are still some defects such as insufficient tensile strength, cold and heat resistance, poor aging resistance, and partial shear stre...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more