Trivalent chromium electroplate liquid capable of forming black clad layer

A technology of trivalent chromium and electroplating solution, which is applied in the field of trivalent chromium electroplating solution, which can solve the problems of poor adhesion, difficult maintenance and complex composition, and achieve the effect of good adhesion, easy maintenance and simple composition

Inactive Publication Date: 2011-02-09
GOOD CHEM SCI & TECH
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing trivalent chromium electroplating solutions that form black coatings have complex components, difficult maintenance, poor adhesion, and often shallow black coatings, which cannot meet the needs of the industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The composition contained in the trivalent chromium electroplating solution that can form a black coating is as shown in table 1:

[0017] Table 1: Components of trivalent chromium electroplating solutions that can form black coatings

[0018] raw material

Embodiment 2

[0020] The composition contained in the trivalent chromium electroplating solution that can form black coating is as shown in table 2:

[0021] Table 2: Components of Trivalent Chromium Electroplating Baths That Can Form Black Plating

[0022] Substance name

[0023] Potassium formate

Embodiment 3

[0025] Form the contained composition of black coating electroplating solution as shown in table 3:

[0026] Table 3: Components of black coating electroplating solution

[0027] Substance name

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses trivalent chromium electroplate liquid capable of forming a black clad layer. Each liter of the trivalent chromium electroplate liquid comprises the following raw materials: a cylinder opening agent, 20 to 150g of stabilizing agent, 10 to 20g of cobalt chloride or manganese chloride, 0.6 to 1.5g of ferric chloride, and 1 to 10g of wetting agent, wherein each liter of cylinder opening agent consists of 5 to 30g of blackening agent, 90 to 140g of chromic salt, 180 to 300g of L conducting salt, 25 to 90g of pH buffering agent. The trivalent chromium electroplate liquid capable of forming the black clad layer has simple components and is easy to maintain; and the formed black clad layer has deep black color and high adhesion.

Description

technical field [0001] The invention relates to a trivalent chromium electroplating solution capable of forming a black coating and an electroplating method using the electroplating solution. Background technique [0002] Hexavalent chromium is an ingestion poison / inhalation extremely poison, skin contact may cause sensitivity; it is more likely to cause hereditary gene defects, inhalation may cause cancer, and has persistent danger to the environment. Hexavalent chromium is gradually being abandoned as an electroplating solution. The toxicity of trivalent chromium is only 1% of hexavalent chromium, the sewage treatment is easy, and the adhesion of the coating formed by the trivalent chromium plating solution is very good, so the trivalent chromium electroplating process has been developed rapidly in recent years. The black chromium plating layer has particularly excellent physical and chemical properties. It not only has a magnificent and solemn decorative appearance, but a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/08
Inventor 李树泉谢金平谢绍俊范小玲
Owner GOOD CHEM SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap